TITLE

c-axis oriented YBa2Cu3O7-x superconducting films by metalorganic chemical vapor deposition

AUTHOR(S)
Zhang, K.; Kwak, B. S.; Boyd, E. P.; Wright, A. C.; Erbil, A.
PUB. DATE
January 1989
SOURCE
Applied Physics Letters;1/23/1989, Vol. 54 Issue 4, p380
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Highly textured single phase superconducting YBa2Cu3O7-x films have been successfully grown on the yttria-stabilized zirconia (100) substrates by using the metalorganic chemical vapor deposition technique. The as-deposited films grown at 650 °C were homogeneous mixtures of the related metal oxides and carbonates. Subsequent thermal annealing under oxygen flow yielded single phase superconducting films whose thickness corresponded to the deposition rates of approximately 10 μm/h. After the post-annealing the films deposited on the yttria-stabilized zirconia substrates exhibited a highly textured x-ray pattern with c axis perpendicular to the substrate surface. These films show an onset superconducting transition temperature of 93 K with the resistance becoming zero at 84 K.
ACCESSION #
9829673

 

Related Articles

  • Preparation of the Tl-Ba-Ca-Cu-O thick film by processing the screen-printed Ba-Ca-Cu-O film in Tl2O3 vapor. Zeng, Lingwen; Zhao, Zijiang; Zhang, Li; Chen, Hongqi; Qian, Zhengnan; Wu, Daiming // Applied Physics Letters;4/16/1990, Vol. 56 Issue 16, p1573 

    Superconducting Tl-Ba-Ca-Cu-O thick films on yttria-stablized zirconia (YSZ) substrates have been obtained by processing the screen-printed Ba-Ca-Cu-O films in Tl2O3 vapor. The properties of the films are found to be dependent sensitively on the Tl2O3 vapor processing conditions. The best film...

  • Deposition of superconducting YBaCuO thin films by pseudospark ablation. Höbel, M.; Geerk, J.; Linker, G.; Schultheiss, C. // Applied Physics Letters;3/5/1990, Vol. 56 Issue 10, p973 

    Thin YBaCuO films have been deposited on ZrO2(Y) and SrTiO3 substrates by a novel ablation method, using a pulsed intense electron beam generated by a pseudospark source. Films with zero resistance around 85 K were grown at substrate temperatures of 820 °C with high reproducibility. X-ray...

  • Superconducting thin films of Bi-Sr-Ca-Cu-O obtained by laser ablation processing. Kim, B. F.; Bohandy, J.; Phillips, T. E.; Green, W. J.; Agostinelli, E.; Adrian, F. J.; Moorjani, K.; Swartzendruber, L. J.; Shull, R. D.; Bennett, L. H.; Wallace, J. S. // Applied Physics Letters;7/25/1988, Vol. 53 Issue 4, p321 

    Thin films of Bi-Sr-Ca-Cu-O, deposited on (100) cubic zirconia by laser ablation from a bulk superconducting target of nominal composition BiSrCaCu2 Ox , have been investigated by dc resistance and magnetically modulated microwave absorption measurements. The latter technique reveals important...

  • Angle-dependent laser-induced voltages in room-temperature polycrystalline wafers of YBa2Cu3O7-x. Tate, K. L.; Hilinski, E. F.; Foster, S. C. // Applied Physics Letters;12/3/1990, Vol. 57 Issue 23, p2407 

    Room-temperature laser-induced voltages were observed in unsupported, polycrystalline wafers of YBa2Cu3O7-x in the absence of a transport current. Peak voltages of ∼1 V were detected in response to 40 mJ pulses of 532 nm light. The rise and fall times for the signals were detector limited....

  • Single-crystal preparation and some characterizations of the superconducting Y-Ba-Cu oxide. Haneda, Hajime; Isobe, Mitsumasa; Hishita, Shunichi; Ishizawa, Yoshio; Shirasaki, Shin-ichi; Yamamoto, Taisei; Yanagitani, Takagimi // Applied Physics Letters;11/30/1987, Vol. 51 Issue 22, p1848 

    Single crystals of Ba2YCu3O7-δ were prepared from melts of a BaO-Y2O3-CuO mixture and characterized by the x-ray microprobe analyzer and x-ray diffraction. Electrical resistivity was measured by the standard four-terminal method. Some crystals have the critical temperature above 77 K. After...

  • Structural characterization of a TlCaBaCu oxide in Tc onset=155 K and Tc zero=123 K superconducting specimens. Liang, J. M.; Liu, R. S.; Chang, L.; Wu, P. T.; Chen, L. J. // Applied Physics Letters;10/10/1988, Vol. 53 Issue 15, p1434 

    The crystal structure of a Tl-Ca-Ba-Cu-O compound in Tc onset=155 K and Tc zero=123 K superconducting specimens was characterized by transmission electron microscopy. Convergent beam electron diffraction analysis established that the phase is of P4/mcc space group. The lattice parameters of the...

  • Properties of Bi(Pb)-Sr-Ca-Cu-O superconducting tapes prepared by the doctor-blade process. Yanagisawa, E.; Morimoto, T.; Dietderich, D. R.; Kumakura, H.; Togano, K.; Maeda, H. // Applied Physics Letters;6/19/1989, Vol. 54 Issue 25, p2602 

    Improved superconducting and mechanical properties were obtained for Bi(Pb)-Sr-Ca-Cu-O tapes, prepared by the combined process of doctor-blade casting, cold rolling, and sintering. The tape has an oriented microstructure with the high Tc plate-like grains having their c axes perpendicular to the...

  • Effect of Li doping on the critical temperature and glass formation in the Bi�Sr�Ca�Cu�O system. Volkov, M. P.; Melekh, B. T.; Bakharev, V. I.; Kartenko, N. F.; Matykin, N. V.; Filin, Yu. N. // Physics of the Solid State;Jan99, Vol. 41 Issue 1, p15 

    A study has been made of the glass-forming ability, structure, and superconducting properties of Bi[sub 2.2]Sr[sub 1.8]Ca[sub 1.05]Cu[sub 2.15]Li[sub x]O[sub y] and Bi[sub 2.2]Sr[sub 1.8]Ca[sub 1.05]Cu[sub 2.15 - x]Li[sub x]O[sub y] (x = 0; 0.3; 0.5; 0.7). The compounds were melted by rf at T =...

  • Synthesis of a Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub y] high-temperature superconducting phase with T[sub c][sup °] above 100 K. Tomilo, Zh. M.; Prytkova, N. A.; Gololobov, E. M.; Turtsevich, D. M. // Technical Physics Letters;Jun97, Vol. 23 Issue 6, p422 

    A high-temperature superconductor with the Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub y] structure and a superconducting transition temperature T[sup º, sub c] = 102-107 K has been synthesized. The synthesis conditions are described and results of a phase analysis, and of resistive and inductive...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics