TITLE

Y-Ba-Cu-O superconducting films prepared on SrTiO3 substrates by chemical vapor deposition

AUTHOR(S)
Yamane, H.; Masumoto, H.; Hirai, T.; Iwasaki, H.; Watanabe, K.; Kobayashi, N.; Muto, Y.; Kurosawa, H.
PUB. DATE
October 1988
SOURCE
Applied Physics Letters;10/17/1988, Vol. 53 Issue 16, p1548
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
High Tc superconducting YBa2 Cu3 O7-x films were prepared by chemical vapor deposition using β-diketonates of Y, Ba, and Cu as source materials. The films were epitaxially grown on SrTiO3 (100) substrates. The c-axis orientation perpendicular to the plane of the substrates was observed. A sharp resistive superconducting transition with Tc (R=0) at 84 K was obtained. The maximum critical-current density at 77 K was 2×104 A/cm2 .
ACCESSION #
9828452

 

Related Articles

  • Formation of oriented high Tc superconducting Bi-Sr-Ca-Cu-O thin films on silver substrates by organometallic chemical vapor deposition. Zhang, J. M.; Wessels, B. W.; Tonge, L. M.; Marks, T. J. // Applied Physics Letters;3/5/1990, Vol. 56 Issue 10, p976 

    Highly oriented thin films of the high Tc Bi-Sr-Ca-Cu-O superconductor have been deposited on silver substrates by low-pressure organometallic chemical vapor deposition. The volatile metalorganic complexes Cu(acetylacetonate)2, Sr(dipivaloylmethanate)2, Ca(dipivaloylmethanate)2, and triphenyl...

  • Preparation of Y-Ba-Cu-O high Tc superconducting thin films by plasma-assisted organometallic chemical vapor deposition. Bai, G. R.; Tao, W.; Wang, R.; Xie, L. M.; Zhang, X. K.; Huang, J.; Qian, C. T.; Zhou, W. K.; Ye, C. Q.; Ren, J. G.; Li, Y. Q.; Luo, W. M.; Chen, J. B. // Applied Physics Letters;7/10/1989, Vol. 55 Issue 2, p194 

    Thin films of the high Tc superconducting Y-Ba-Cu metal oxide have been prepared for the first time by plasma-assisted organometallic chemical vapor deposition using β-diketonate chelates of Y, Ba, and Cu, Y(C11H19O2)3, Ba(C11H19O2)2, and Cu(C11H19O2)2 as starting materials, followed by...

  • Growth of Ultrathin YBa[sub 2]Cu[sub 3]O[sub 7 – ][sub x] Films on the SrTiO[sub 3] Substrate. Gol’man, E. K.; Il’in, R. N.; Plotkin, D. A.; Razumov, S. V.; Sakharov, V. I.; Serenkov, I. T. // Physics of the Solid State;Mar2000, Vol. 42 Issue 3, p406 

    The growth of ultrathin (1.7-7.3 nm)YBa[sub 2]Cu[sub 3]O[sub 7-x] films on the SrTiO[sub 3](100) substrate is investigated by the mean-energy ion scattering technique. It is found that the growth of islands proceeds according to the two-dimensional and three-dimensional models and depends on the...

  • Superheating of YBa[sub 2]Cu[sub 3]O[sub 7-x] thin-film microbridges. Matyunina, O. V.; Pogrebnyakov, A. V. // Technical Physics Letters;Jun97, Vol. 23 Issue 6, p478 

    It is found that the hysteresis that develops with decreasing temperature in the current-voltage characteristics of thin-film YBa[sub 2]Cu[sub 3]O[sub 7-x] microbridges is due to superheating of the bridges by the transport current. The heat transport coefficient is determined to be...

  • Photoelectron spectra of thin films of the high-T[sub c] superconductor YBa[sub 2]Cu[sub 3]O[sub 7-δ]. Likhachev, E. R.; Kurganskiı, S. I.; Dubrovskiı, O. I.; Bugakov, A. M. // Physics of the Solid State;Mar97, Vol. 39 Issue 3, p378 

    The results of calculations of the energy band structure of thin films are used to obtain theoretical photoelectron spectra of the valence band of the compound YBa[sub 2]Cu[sub 3]O[sub 7-δ] for δ=0 and δ=1 at various photon energies; the spectra are averaged over the photoelectron...

  • A broadband method for the measurement of the surface impedance of thin films at microwave frequencies. Booth, J. C.; Wu, Dong Ho; Anlage, Steven M. // Review of Scientific Instruments;Jun94, Vol. 65 Issue 6, p2082 

    We present a new technique to measure the complex surface impedance of the mixed state of superconducting thin films over the broad frequency range 45 MHz-20 GHz. The surface impedance is extracted from measurements of the complex reflection coefficient made on the film using a vector network...

  • Magnetotransport Properties of GdBa[sub 2]Cu[sub 3]O[sub 7 - δ] Superconducting Thin Films. Roa-Rojas, J.; Téllez, D. A. Landínez; Prieto, P. // Surface Review & Letters;Oct-Dec2002, Vol. 9 Issue 5/6, p1791 

    Systematic measurements of the Hall and longitudinal resistivities as a function of temperature in GdBa[sub 2]Cu[sub 3]O[sub 7-δ] thin films were effectuated. These were performed in magnetic fields B = 0, 1, 2, 3, 4 and 5 T, applied perpendicular to the transport current orientation. Films...

  • Surface Topography on Epitaxial HoBa[sub 2]Cu[sub 3]O[sub 7-δ] and Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub 8+δ] Thin Films. Lopera, W.; Giratá, D.; Pérez, F.; Castro, L. F.; Baca, E.; Prieto, P.; Mendoza, A. // Surface Review & Letters;Oct-Dec2002, Vol. 9 Issue 5/6, p1729 

    Surface topography on epitaxial HoBa[sub 2]Cu[sub 3]O[sub 7-δ] (HBCO) and Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub 8+δ] (BSCCO) thin films analysis by using the atomic force microscopy (AFM) technique was carried out. The films were deposited in situ on SrTiO[sub 3] substrates with thicknesses...

  • Preparation of NdBa2Cu3O7-δ films in ultrahigh vacuum with a NO2 supersonic molecular beam. Nonaka, Hidehiko; Shimizu, Takashi; Arai, Kazuo // Applied Physics Letters;12/24/1990, Vol. 57 Issue 26, p2850 

    Superconducting NdBa2Cu3O7-δ thin films have been prepared in ultrahigh vacuum by the molecular beam epitaxy (MBE) method using a supersonic molecular beam of nitrogen dioxide as an oxidizing agent. A new type of supersonic molecular beam source has been developed, which has a liquid nitrogen...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics