TITLE

Highly oriented superconducting Tl-Ca-Ba-Cu oxide thin films with 2-1-2-2 phase

AUTHOR(S)
Ichikawa, Yo; Adachi, Hideaki; Setsune, Kentaro; Hatta, Shin-ichiro; Hirochi, Kumiko; Wasa, Kiyotaka
PUB. DATE
September 1988
SOURCE
Applied Physics Letters;9/5/1988, Vol. 53 Issue 10, p919
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Thin films of the Tl-Ca-Ba-Cu-O system with 2-1-2-2 phase have been prepared stably on MgO substrates by rf magnetron sputtering and post-annealing. The post-annealing of the films was carefully carried out in order to reduce the effect of evaporation of Tl. The annealed films showed a c-axis-oriented structure perpendicular to the substrates. The highest zero-resistance temperature of the films was 102 K. The highest critical current density obtained so far was 1.2×105 A/cm2 at 77 K.
ACCESSION #
9827947

 

Related Articles

  • Electrical-transport properties and microwave device performance of sputtered TlCaBaCuO superconducting thin films. Subramanyam, G.; Kapoor, V. J.; Chorey, C. M.; Bhasin, K. B. // Journal of Applied Physics;9/15/1992, Vol. 72 Issue 6, p2396 

    Presents a study that examined thallium-calcium-barium-copper-oxygen superconducting thin films deposited on lanthanum aluminate substrates. Use of radio frequency magnetron sputtering and postannealing methods; Importance of copper-oxide high transition temperature superconductors; Information...

  • Preparation of superconducting Tl-Ca-Ba-Cu thin films by chemical deposition. Olson, William L.; Eddy, Michael M.; James, Tim W.; Hammond, Robert B.; Gruner, George; Drabeck, Larry // Applied Physics Letters;7/10/1989, Vol. 55 Issue 2, p188 

    A chemical deposition process for the preparation of superconducting thin films of Tl2CaBa2Cu2O8 (2122) and Tl2Ca2Ba2Cu3O10 (2223) has been developed. Oriented, superconducting 2122 and 2223 thin films have been successfully fabricated on single-crystal yttria-stabilized zirconia and magnesium...

  • Superconducting Tl-Ca-Ba-Cu-O thin films with zero resistance at temperatures of up to 120 K. Lee, W. Y.; Lee, V. Y.; Salem, J.; Huang, T. C.; Savoy, R.; Bullock, D. C.; Parkin, S. S. P. // Applied Physics Letters;7/25/1988, Vol. 53 Issue 4, p329 

    We have prepared superconducting Tl-Ca-Ba-Cu-O thin films on a variety of substrates with transition temperatures as high as [bar_over_tilde:_approx._equal_to]120 K, confirmed by sharp onsets of substantial Meissner and shielding signals at the same temperatures. The properties of the films are...

  • Crystallography and microstructure of Tl-Ca-Ba-Cu-O superconducting oxides. Beyers, R.; Parkin, S. S. P.; Lee, V. Y.; Nazzal, A. I.; Savoy, R.; Gorman, G.; Huang, T. C.; La Placa, S. // Applied Physics Letters;8/1/1988, Vol. 53 Issue 5, p432 

    We report on the crystallography and microstructure of six oxides in the Tl-Ca-Ba-Cu-O system with nominal compositions Tl1Ba2Cu1O5, Tl1Ca1Ba2Cu2O7, Tl1Ca2Ba2Cu3O9, Tl2Ba2Cu1O6, Tl2Ca1Ba2Cu2O8, and Tl2Ca2Ba2Cu3O10. The structures consist of one, two, or three Cu perovskite-like units sandwiched...

  • Structural characterization of a TlCaBaCu oxide in Tc onset=155 K and Tc zero=123 K superconducting specimens. Liang, J. M.; Liu, R. S.; Chang, L.; Wu, P. T.; Chen, L. J. // Applied Physics Letters;10/10/1988, Vol. 53 Issue 15, p1434 

    The crystal structure of a Tl-Ca-Ba-Cu-O compound in Tc onset=155 K and Tc zero=123 K superconducting specimens was characterized by transmission electron microscopy. Convergent beam electron diffraction analysis established that the phase is of P4/mcc space group. The lattice parameters of the...

  • Anisotropic transport and cation disorder in superconducting Tl2Ca2Ba2Cu3Ox single crystals. Tigges, C. P.; Venturini, E. L.; Kwak, J. F.; Morosin, B.; Baughman, R. J.; Ginley, D. S. // Applied Physics Letters;7/30/1990, Vol. 57 Issue 5, p517 

    We have measured for the first time the temperature-dependent anisotropic resistivity of several Tl2Ca2Ba2Cu3Ox single crystals. The resistivity ratio between the c axis and the a-b plane orientations in the best crystals is approximately 60 at room temperature. Resistivity data indicate...

  • Superconducting contacts for use in niobium thin film applications. Garfield, James R.B. // Review of Scientific Instruments;Apr97, Vol. 68 Issue 4, p1906 

    Describe a simple method for forming superconducting contacts to niobium thin films as used for current perpendicular to the plane measurements of the resistance of magnetic multilayers using an indium-Roses alloy. Measurement of the superconducting transition temperature; Cooling of samples;...

  • Influence of working gas pressure on the properties of thin films of high-temperature superconductors obtained by magnetron sputtering. Vorob’ev, A. K.; Gaponov, S. V.; Gusev, S. A.; Drozdov, Yu. N.; Klyuenkov, E. B.; Luchin, V. I. // Technical Physics Letters;Feb98, Vol. 24 Issue 2, p159 

    The surface morphology, composition, microstructure, and electrical properties of thin films of YBa[sub 2]Cu[sub 3]O[sub 7-x] high-temperature superconductors, obtained by inverted magnetron sputtering, have been studied as a function of the pressure of the working gas mixture and results are...

  • Features of the microwave breakdown of a high-T[sub c] superconducting film at defects. Buznikov, N. A.; Pukhov, A. A. // Technical Physics Letters;Sep98, Vol. 24 Issue 9, p697 

    The influence of nonsuperconducting defects on the power density for microwave breakdown of a high-T[sub c] superconducting film is investigated theoretically. It is found that the scenario of the destruction of superconductivity depends substantially on the shape of the defect and on the ratio...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics