YBaCuO superconducting films on SiO2 substrates formed from Cu/BaO/Y2O3/Ag layer structures

Chang, Chin-An; Tsuei, C. C.; McGuire, T. R.; Yee, D. S.; Boresh, J. P.; Lilienthal, H. R.; Farrell, C. E.
September 1988
Applied Physics Letters;9/5/1988, Vol. 53 Issue 10, p916
Academic Journal
Cu/BaO/Y2O3/Ag layer structures were deposited on SiO2 substrates at 600 °C and post-annealed in oxygen at different temperatures. Superconducting oxides with a thickness of 5000 Å were formed at 800 °C, with an onset of 92 K and a zero resistance at 70 K. The films contain mainly the YBa2Cu3O7 phase, with the 103 and 020 diffraction peaks being the major ones observed. The high deposition temperature used is shown to help the formation of the YBa2Cu3O7 phase, leading to the observed superconductivity using SiO2 substrates.


Related Articles

  • Features of the microwave breakdown of a high-T[sub c] superconducting film at defects. Buznikov, N. A.; Pukhov, A. A. // Technical Physics Letters;Sep98, Vol. 24 Issue 9, p697 

    The influence of nonsuperconducting defects on the power density for microwave breakdown of a high-T[sub c] superconducting film is investigated theoretically. It is found that the scenario of the destruction of superconductivity depends substantially on the shape of the defect and on the ratio...

  • Superconducting Properties of LuNi[sub 2]B[sub 2]C Thin Films. Grassano, G.; Cimberle, M. R.; Marrè, D.; Pallecchi, I.; Putti, M.; Ramadan, W.; Siri, A. S.; Ferdeghini, C.; Andreone, A.; Cassinese, A.; di Capua, R.; Gianni, L.; Iavarone, M.; Miletto, F.; Ricci, F.; Scotti di Uccio, U.; Vaglio, R.; Canepa, F. // International Journal of Modern Physics B: Condensed Matter Phys;10/30/2000, Vol. 14 Issue 25/27, p2743 

    We present the results of collaboration between the groups of Naples and Genoa Universities/INFM, focused on thin films superconducting borocarbides. In particular a careful study of the deposition of non-magnetic LuNi[sub 2]B[sub 2]C thin films by Pulsed Laser Deposition (PLD) on MgO and other...

  • On the Role of Nd/Ba Disorder on the Superconducting Properties of Re[sub 1](Nd[sub x]Ba[sub 2-x])Cu[sub 3]O[sub 7-δ](Re=Nd, Y) Thin Films. Salluzzo, M.; Andreone, A.; Cassinese, A.; Iavarone, M.; Maglione, M. G.; Palomba, F.; Pica, G.; Vaglio, R. // International Journal of Modern Physics B: Condensed Matter Phys;10/30/2000, Vol. 14 Issue 25/27, p2737 

    The role of disorder on the superconducting properties of Re[sub 1](Nd[sub x]Ba[sub 2-x])Cu[sub 3]0[sub 7-δ] (Re = Nd, Y) epitaxial thin films has been studied. The films are deposited by Ar+O[sub 2] magnetron and diode dc sputtering from targets characterised by different x (0, 0.08, and...

  • Preparation, patterning, and properties of thin YBa2Cu3O7-δ films. de Vries, J. W. C.; Dam, B.; Heijman, M. G. J.; Stollman, G. M.; Gijs, M. A. M.; Hagen, C. W.; Griessen, R. P. // Applied Physics Letters;5/30/1988, Vol. 52 Issue 22, p1904 

    High TC superconducting thin films were prepared on (100) SrTiO3 substrates by dc triode sputtering and subsequent annealing. In these films Hall-bar structures having a width down to 5 μm were patterned using a reactive ion etching technique. Superconductivity above 77 K was observed. When...

  • Superconducting Y1Ba2Cu3O7-x films on Si. Venkatesan, T.; Chase, E. W.; Wu, X. D.; Inam, A.; Chang, C. C.; Shokoohi, F. K. // Applied Physics Letters;7/18/1988, Vol. 53 Issue 3, p243 

    By depositing YBaCuO films at low substrate holder temperatures (600 °C) using a pulsed laser, films with the orthorhombic phase exhibiting superconductivity with high zero resistance temperatures (Tc0) were produced. Tc0 values as high as 50 and 80 K were seen on films deposited directly on...

  • Deposition of superconducting Y-Ba-Cu-O films at 400 °C without post-annealing. Witanachchi, S.; Kwok, H. S.; Wang, X. W.; Shaw, D. T. // Applied Physics Letters;7/18/1988, Vol. 53 Issue 3, p234 

    Superconducting thin films of Y1Ba2Cu3O7-x were fabricated using the process of plasma-assisted laser deposition. The substrate temperature was as low as 400 °C and high-temperature post-annealing in an O2 atmosphere was not necessary. The as-deposited films have a Tc of ∼85 K, and are...

  • Effects of coexisting nonsuperconducting phase on the superconductivity of YBa2Cu3O7. Itoh, Takao; Uchikawa, Hiroshi // Journal of Applied Physics;11/15/1989, Vol. 66 Issue 10, p4900 

    Deals with a study which investigated the effects of coexisting nonsuperconducting phases on the superconductivity of a thin film. Methodology of the study; Results and discussion.

  • X-ray irradiation effects on superconductivity of cuprate superconductor thin films. Kohiki, Shigemi; Hatta, Shin-ichiro; Setsune, Kentaro; Wasa, Kiyotaka; Sakai, Masahiro; Fukushima, Sei; Gohshi, Yoichi // Journal of Applied Physics;12/1/1991, Vol. 70 Issue 11, p6945 

    X-ray irradiation effects on superconductivity of cuprate superconductor thin films. Method of the study; Results and discussion; Conclusion.

  • Growth and superconducting properties of YBa[sub 2]Cu[sub 3]O[sub 7-δ] films on conductive SrRuO[sub 3] and LaNiO[sub 3] multilayers for coated conductor applications. Aytug, T.; Wu, J. Z.; Wu, J.Z.; Cantoni, C.; Verebelyi, D. T.; Verebelyi, D.T.; Specht, E. D.; Specht, E.D.; Paranthaman, M.; Norton, D. P.; Norton, D.P.; Christen, D. K.; Christen, D.K.; Ericson, R. E.; Ericson, R.E.; Thomas, C. L.; Thomas, C.L. // Applied Physics Letters;2/7/2000, Vol. 76 Issue 6 

    Conductive multilayers of YBa[sub 2]Cu[sub 3]O[sub 7-δ]/SrRuO[sub 3]/LaNiO[sub 3] (YBCO/SRO/LNO), YBCO/SRO, and YBCO/LNO were grown epitaxially on single-crystal LaAlO[sub 3] and SrTiO[sub 3] substrates. Property characterizations revealed that the YBCO films on SRO and SRO/LNO buffer...


Read the Article


Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics