TITLE

Preparation of superconducting Y-Ba-Cu-O thick films with preferred c-axis orientation by a screen-printing method

AUTHOR(S)
Tabuchi, Junji; Utsumi, Kazuaki
PUB. DATE
August 1988
SOURCE
Applied Physics Letters;8/15/1988, Vol. 53 Issue 7, p606
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Superconducting Y-Ba-Cu-O thick films with preferred c-axis orientation were obtained by a screen-printing method. Thick films with preferred c-axis orientation appeared only when the substrate material was YSZ, the film thickness was around 10 μm, and the film was fired at 980 °C for 6 min. The preferred c-axis orientation was caused by an interface reaction between the Y-Ba-Cu-O thick film and the YSZ substrate. The superconducting characteristics of the thick film were T zeroc =89 K and Jc (77 K)=7 A/cm2 .
ACCESSION #
9827693

 

Related Articles

  • Superconducting Bi-cuprate thick film T[sub c(0)]=110 K on DyBa[sub 2]SnO[sub 5.5]: A newly.... Koshy, J.; Kumar, K.S. // Applied Physics Letters;11/28/1994, Vol. 65 Issue 22, p2857 

    Presents the synthesis and development of DyBa[sub 2]SnO[sub 5.5] (DBSO) perovskite substrate and the fabrication of superconducting bismuth (Bi) thick film on the substrate. Use of the dielectric constant and loss factor for microwave application; Compatibility of DBSO with Bi(Pb)-Sr-Ca-CuO...

  • High Tc screen-printed YBa2Cu3O7-x films: Effect of the substrate material. Bansal, Narottam P.; Simons, Rainee N.; Farrell, D. E. // Applied Physics Letters;8/15/1988, Vol. 53 Issue 7, p603 

    Thick films of YBa2Cu3O7-x have been deposited on highly polished alumina, magnesia spinel, nickel aluminum titanate (Ni-Al-Ti), and barium tetratitanate (Ba-Ti) substrates by the screen printing technique. They were baked at 1000 °C for 15 min, oxygen annealed at a lower temperature, and...

  • Y-Ba-Cu-O superconducting film on oxidized silicon. Gupta, Ram P.; Khokle, W. S.; Dubey, R. C.; Singhal, Seema; Nagpal, K. C.; Rao, G. S. T.; Jain, J. D. // Applied Physics Letters;6/6/1988, Vol. 52 Issue 23, p1987 

    We report thick superconducting films of Y-Ba-Cu-O on oxidized silicon substrates. The critical temperatures for onset and zero resistance are 96 and 77 K, respectively. X-ray diffraction analysis predicts 1, 2, 3 composition and orthorhombic phase of the film.

  • Preparation and transport properties of high-Tc superconducting thick films. Aponte, J. M.; Octavio, M. // Journal of Applied Physics;8/1/1989, Vol. 66 Issue 3, p1480 

    Presents information on a study which prepared thick films of high T[subc] superconductors on a variety of substrates. Use of superconducting ceramics in hybrid circuits; Measurements performed in a closed-cycle refrigerator with temperature control from room temperature; Fabrication of samples...

  • Tl[sub 2]Ba[sub 2]CaCu[sub 2]O[sub 8] films with very low microwave surface resistance up to 95 K. Holstein, W.L.; Parisi, L.A. // Applied Physics Letters;4/20/1992, Vol. 60 Issue 16, p2014 

    Analyzes the high-temperature superconductor thick films with very low microwave surface resistance. Preparation of the films; Ways to measure the precursor film composition; Measurement of the surface resistance with the parallel plate resonator technique.

  • Deposition of thick YBa[sub 2]Cu[sub 3]O[sub 7-x] films on sapphire with a sublayer of cerium oxide. Hollmann, E. K.; Gol’drin, V. I.; Loginov, V. E.; Plotkin, D. A.; Razumov, S. V.; Tumarkin, A. V. // Technical Physics Letters;Mar97, Vol. 23 Issue 3, p186 

    A report is made on the results of experiments to prepare YBa[sub 2]Cu[sub 3]O[sub 7-x] films up to 2.6 µm thick on Al[sub 2]O[sub 3]/CeO[sub 2] with good structural perfection and electrophysical parameters.

  • The microwave surface impedance of granular high TC superconductors in dc magnetic fields: Its relationship to frequency dependence. Remillard, S. K.; Reeves, M. E.; Rachford, F. J.; Wolf, S. A. // Journal of Applied Physics;4/15/1994, Vol. 75 Issue 8, p4103 

    Presents information on a study which examined the surface impedance of bulk and thick film granular high temperature superconductors. Analysis of the weakly coupled grain model; Methodology of the study; Results and discussion.

  • Generalized proximity effect model in superconducting bi- and trilayer films. Brammertz, G.; Poelaert, A.; Golubov, A. A.; Verhoeve, P.; Peacock, A.; Rogalla, H. // Journal of Applied Physics;7/1/2001, Vol. 90 Issue 1, p355 

    This article presents a general model for calculating the density of states and the Cooper pair potential in proximity-coupled superconducting bi- and trilayer films. It is valid for any kind of bilayer S[sub 1]-S[sub 2], whatever the quality of the materials S[sub 1] and S[sub 2], the quality...

  • Fabrication and properties of textured YBa2Cu3O7 thick films on polycrystalline Ag0.9Pd0.1 and silver substrates. Wang, Y.-L.; Wiesmann, H. J.; Liu, C. F.; Zhu, Y.; Sabatini, R. L.; Suenaga, M. // Journal of Applied Physics;9/15/1993, Vol. 74 Issue 6, p4052 

    Presents a study which fabricated highly textured thick films of YBa[sub2]Cu[sub3]O[sub7] (YBCO) (123) grown on Ag[0.9]Pd[0.1] and pure silver substrates by a traveling heated zone method. Information on the transport critical current density of thick films; Discussion on the superconducting...

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics