TITLE

Direct laser writing of superconducting patterns of Y1Ba2Cu3O7-δ

AUTHOR(S)
Gupta, Arunava; Koren, Gad
PUB. DATE
February 1988
SOURCE
Applied Physics Letters;2/22/1988, Vol. 52 Issue 8, p665
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Direct argon ion laser writing of 40-μm-wide and 3-μm-thick superconducting lines of Y1Ba2Cu3O7-δ on magnesium oxide (MgO) substrate is reported. A 514.5 nm laser beam of 300 mW was focused onto a thin sprayed film of the nitrate precursors (Y:Ba:Cu=1:2:3) and scanned over it. The laser beam converted oxides along the irradiation path. The film was then ‘‘developed’’ by rinsing it in ethanol, which removed the unirradiated areas, but left the irradiated areas intact. This was followed by the standard oven annealing procedure in flowing oxygen. The resistivity of the laser-written lines as a function of temperature showed an onset and completion of the superconducting transition at 82 and 69 K, respectively. The corresponding values of the unpatterned, blanket film were 82 and 77 K, respectively.
ACCESSION #
9826006

 

Related Articles

  • Effect of Li doping on the critical temperature and glass formation in the Bi–Sr–Ca–Cu–O system. Volkov, M. P.; Melekh, B. T.; Bakharev, V. I.; Kartenko, N. F.; Matykin, N. V.; Filin, Yu. N. // Physics of the Solid State;Jan99, Vol. 41 Issue 1, p15 

    A study has been made of the glass-forming ability, structure, and superconducting properties of Bi[sub 2.2]Sr[sub 1.8]Ca[sub 1.05]Cu[sub 2.15]Li[sub x]O[sub y] and Bi[sub 2.2]Sr[sub 1.8]Ca[sub 1.05]Cu[sub 2.15 - x]Li[sub x]O[sub y] (x = 0; 0.3; 0.5; 0.7). The compounds were melted by rf at T =...

  • Synthesis of a Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub y] high-temperature superconducting phase with T[sub c][sup °] above 100 K. Tomilo, Zh. M.; Prytkova, N. A.; Gololobov, E. M.; Turtsevich, D. M. // Technical Physics Letters;Jun97, Vol. 23 Issue 6, p422 

    A high-temperature superconductor with the Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub y] structure and a superconducting transition temperature T[sup º, sub c] = 102-107 K has been synthesized. The synthesis conditions are described and results of a phase analysis, and of resistive and inductive...

  • Nd[sub 2]CuO[sub 4]: Chirality and its effect on optical and acoustic properties. Turov, E. A. // Journal of Experimental & Theoretical Physics;Apr99, Vol. 88 Issue 4, p766 

    It is shown that two possible magnetic structures in the exchange doublet of the exchangenoncollinear antiferromagnetic material Nd[sub 2]CuO[sub 4] that are distinguished by their chirality have certain differences in their optical and acoustic properties. These differences make it possible to...

  • Thermopower and Resistivity in the Normal State of Mercury Cuprate HTSCs under Pressure. Itskevich, E. S.; Kraıdenov, V. F.; Kuzemskaya, I. G. // Journal of Experimental & Theoretical Physics;Sep2000, Vol. 91 Issue 3, p562 

    Nonmonotonic temperature dependence of the thermopower and resistivity of the multilayer mercury cuprate HgBa[sub 2]Ca[sub 4]Cu[sub 5]O[sub 12] are observed in the temperature range 77-300 K under hydrostatic pressures of up to 10 kbar. The data obtained agree qualitatively with our results for...

  • Practical preparation of copper oxide superconductors. Chen, Xiao-Dong; Lee, Sang Young; Golben, John P.; Lee, Sung-Ik; McMichael, R. D.; Song, Yi; Noh, Tae W.; Gaines, J. R. // Review of Scientific Instruments;Sep87, Vol. 58 Issue 9, p1565 

    We present a thorough yet simple approach for synthesizing high Tc superconductors of substantial quality. The approach is accompanied by a step-by-step discussion of possible pitfalls as well as a correlation of the sample characteristics to the various preparation procedures. A procedure...

  • Transport properties of high-temperature superconductor + semiconductor composites with different carrier concentration. Petrov, M. I.; Balaev, D. A.; Shaıkhutdinov, K. A.; Khrustalev, B. P.; Aleksandrov, K. S. // Physics of the Solid State;May97, Vol. 39 Issue 5, p735 

    Results are presented of an experimental study of the temperature dependence of the electrical resistivity ρ(T), critical current density J[sub c](T), and current-voltage characteristics of polycrystalline composites based on the high-temperature superconductor Y[sub 3/4]Lu[sub 1/4]Ba[sub...

  • Effect of a pulsed magnetic field on the transverse resistance of a layered superconductor. Zavaritskiı, V. N.; Springford, M. // JETP Letters;9/10/98, Vol. 68 Issue 5, p448 

    The field dependences of the transverse resistance of a single crystal of the layered superconductor Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub y] (BSCCO-2212) with T[sub c0]=92 K are studied in magnetic fields up to 50 T in the perpendicular orientation H⊥(ab). It is established that in the...

  • Anomalous millimeter-wave absorption in the superconducting phase of La[sub 2-x]Sr[sub x]CuO[sub 4]. Pronin, A. V.; Gorshunov, B. P.; Volkov, A. A.; Somal, H. S.; van der Marel, D.; Feenstra, B. J.; Jaccard, Y.; Locquet, J.-P. // JETP Letters;9/10/98, Vol. 68 Issue 5, p432 

    Direct measurements of the complex conductivity spectra of thin-film La[sub 2-x]Sr[sub x]CuO[sub 4] are made at frequencies of 5–40 cm[sup -1]. Narrow, intense Drude-type excitation is observed in the superconducting phase. © 1998 American Institute of Physics.

  • Effect of Silver Content on the Mechanical and Electrical Properties of the YBaCuO/Ag Ceramic. Markov, L.K.; Orlova, T.S.; Peschanskaya, N.N.; Smirnov, B.I.; Stepanov, Yu.P.; Shpeizman, V.V. // Physics of the Solid State;Sep2003, Vol. 45 Issue 9, p1629 

    Doping the YBaCuO superconducting ceramic with 3–5 wt % silver is shown to substantially increase its microplasticity and strength. Temperature spectra of microplastic strain rates for YBaCuO/Ag ceramics with 0, 1.6, 2.9, 4.2, and 7.6 wt % silver were obtained. The structure of the...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics