Superconducting Y-Ba-Cu-O oxide films by sputtering

AUTHOR(S)
Hong, M.; Liou, S. H.; Kwo, J.; Davidson, B. A.
PUB. DATE
August 1987
SOURCE
Applied Physics Letters;8/31/1987, Vol. 51 Issue 9, p694
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
We have prepared superconducting thin films of Y-Ba-Cu-O with Tc onsets above 95 K by both diode and magnetron sputtering. Films with full superconductivity (R=0) at 85 K have been produced by dc magnetron sputtering. The compositions of the films are fairly uniform across an area 50 mm in diameter and through the film thickness. Structural properties of the films were studied by x-ray diffraction. Critical current densities in the range of 3000 to 104 A/cm2 have been measured at 4.2 K.
ACCESSION #
9824031

 

Related Articles

  • Bi-Sr-Ca-Cu-oxide superconducting thin films deposited by dc magnetron sputtering. Sullivan, Brian T.; Osborne, N. R.; Hardy, W. N.; Carolan, J. F.; Yang, B. X.; Michael, P. J.; Parsons, R. R. // Applied Physics Letters;6/6/1988, Vol. 52 Issue 23, p1992 

    Thin films of the high-temperature superconductor Bi-Sr-Ca-Cu-oxide were deposited by dc magnetron sputtering onto various substrates. Films deposited on (100) MgO substrates achieved zero resistance between 78 and 82.5 K depending upon the annealing conditions. The best films were produced with...

  • High critical field anisotropy of superconducting Bi-Sr-Ca-Cu oxide from highly oriented thin films. Kang, J. H.; Kampwirth, R. T.; Gray, K. E. // Applied Physics Letters;6/13/1988, Vol. 52 Issue 24, p2080 

    Superconducting films of Bi-Sr-Ca-Cu oxides have been grown on MgO substrates by multitarget magnetron sputtering. After post-annealing in an oxygen atmosphere, zero resistance was obtained at about 80 K. X-ray diffraction indicates a high degree of preferential growth of the c axis...

  • In situ low-temperature deposition and properties of Bi(Pb)-Sr-Ca-Cu-O thin films prepared by magnetron sputtering. Jedamzik, D.; Barnard, B. R.; Harrison, M. R.; Freeman, W. G.; Howard, P. J. // Applied Physics Letters;4/2/1990, Vol. 56 Issue 14, p1371 

    Superconducting thin films of the Bi-Sr-Ca-Cu-O system with and without lead doping were prepared by rf magnetron sputtering onto (100)MgO substrates. Although the superconducting properties of the thin films are very sensitive to the deposition and soak temperatures, reproducible results were...

  • Microstructures of Sputtered Oriented Si/CeO[sub 2] Bilayers YBa[sub 2]Cu[sub 3]O[sub 7-δ]/Si Integrated Microelectronics. Chiodoni, A.; Mezzetti, E.; Botta, D.; Gozzelino, L.; Minetti, B.; Pirri, C. F.; Tresso, E.; Camerlingo, C.; Tallarida, G.; Barucca, G.; Fabbri, F. // International Journal of Modern Physics B: Condensed Matter Phys;3/10/2003, Vol. 17 Issue 4-6, p848 

    In the framework of a research aimed to superconductor/semiconductor integrated electronics, we have grown a-axis oriented YBa[SUB2]Cu[SUB3]O[SUB7-δ] (YBCO) thin films on silicon (100) substrates with (111) oriented insulating buffer layers of cerium dioxide (CeO[SUB2]), using magnetron...

  • As-grown superconducting Bi(-Pb)-Sr-Ca-Cu-O films by electron cyclotron resonance plasma sputtering. Masumoto, H.; Goto, T.; Hirai, T. // Applied Physics Letters;7/31/1989, Vol. 55 Issue 5, p498 

    Bi(-Pb)-Sr-Ca-Cu-O thin films were prepared on MgO(100) single-crystal substrates by electron cyclotron resonance (ECR) plasma sputtering at substrate temperatures from room temperature to 590 °C. Pb-doped superconducting as-grown films were obtained above 560 °C. The Tc values of the...

  • Absence of negative ion effects during on-axis single target sputter depositions of Y-Ba-Cu-O thin films on Si (100). Migliuolo, M.; Belan, R. M.; Brewer, J. A. // Applied Physics Letters;6/18/1990, Vol. 56 Issue 25, p2572 

    Stoichiometric thin films of YBa2Cu3O7-δ have been deposited on (100) silicon substrates by on-axis single target magnetron sputtering. The effect of oxygen resputtering was minimized through the use of much stronger than usual magnetic assemblies in the source. A magnet assembly...

  • High temperature superconducting YBa[sub 2]Cu[sub 3]O[sub 7-x] films on metallic substrates.... Jia, Q.X.; Anderson, W.A. // Applied Physics Letters;5/25/1992, Vol. 60 Issue 21, p2689 

    Examines the deposition of superconducting YBCO thin films on metallic substrates using the off-axis rf magnetron sputtering. Reduction of the interdiffusion between the substrate and YBCO; Observation of the surface morphology of the films; Achievement of stoichiometric TBCO thin films.

  • In situ growth of superconducting YBa[sub 2]Cu[sub 3]O[sub 7-delta] thin films by a hot-wall.... Lin, R.J.; Chen, L.J. // Applied Physics Letters;1/4/1993, Vol. 62 Issue 1, p105 

    Examines the in situ growth of superconducting YBa[sub 2]Cu[sub 3]O[sub 7-x] thin films. Use of a modified high pressure direct current planar diode sputtering process; Characterization of the film surface; Production of superconducting thin films at a substrate temperature.

  • In situ growth of epitaxial YBa[sub 2]Cu[sub 3]O[sub 7] thin films by on-axis unbalanced direct.... Savvides, N.; Katsaros, A. // Applied Physics Letters;2/1/1993, Vol. 62 Issue 5, p528 

    Describes the growth of epitaxial YBa[sub 2]Cu[sub 3]O[sub 7] superconducting thin films by on-axis direct-current magnetron sputtering. Use of an unbalance magnetic field configuration; Dependence of film growth and properties on sputtering pressure and substrate temperature; Advantages of the...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics