TITLE

Effect of heat treatments on the electrical resistivity of polycrystalline silicon films implanted with antimony

AUTHOR(S)
Komem, Y.; Harrison, H. B.
PUB. DATE
May 1987
SOURCE
Applied Physics Letters;5/25/1987, Vol. 50 Issue 21, p1524
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Polycrystalline silicon films, ion implanted with antimony to a dose of 1–3×1015/cm2 at an energy of 100 keV, were heat treated by means of rapid thermal or conventional furnace techniques. It was found that the electrical resistivity is a function of time, reaching a minimum value that is relatively lower at 600 than 900 °C for heat treatment times that are short enough to avoid significant lattice diffusion, and then increasing with time. However, in cases where longer times at high temperatures (between 860 and 975 °C) are used in order to provide sufficient atom movement, the resistivity increases with decrease in temperature. The results are explained on the basis of recrystallization, diffusion, and segregation processes.
ACCESSION #
9823026

 

Related Articles

  • Polycrystalline silicon films doped with aluminum during deposition. Shengurov, D. V. // Technical Physics Letters;Jun97, Vol. 23 Issue 6, p450 

    Aluminum-doped polycrystalline silicon films have been grown by molecular-beam deposition at substrate temperatures between 540 and 600 °C. The grain size increases to 1-8 µm with increasing substrate temperature. High Hall mobilities of the carriers were measured, in the range 30-90...

  • Morphological instability of NiSi1-uGeu on single-crystal and polycrystalline Si1-xGex. Seger, J.; Jarmar, T.; Z.-B. Zhang; Radamson, H. H.; Ericson, F.; Smith, U.; Zhang, S.-L. // Journal of Applied Physics;8/15/2004, Vol. 96 Issue 4, p1919 

    The morphological stability of NiSi1-uGeu ternary alloy films formed by reacting Ni with single-crystal (sc) and polycrystalline (poly) Si1-xGeu is studied (u can be different from x). The agglomeration of NiSi1-uGeu films on Si0.7Ge0.3 occurs at 550°C after rapid thermal processing for 30 s,...

  • Direct observation of self-focusing near the diffraction limit in polycrystalline silicon film. Choi, Yunjin; Park, June-H.; Kim, Myong R.; Jhe, Wonho; Rhee, Bum Ku // Applied Physics Letters;2/12/2001, Vol. 78 Issue 7, p856 

    We present direct observation of self-focusing near the diffraction limit by measuring the beam-spot size with a scanning fiber probe tip. We have used the polycrystalline silicon film, which exhibits a reverse-saturation (Im χ[sup (3)]approx. 8x10[sup -3] esu) and self-focusing (Re...

  • Dose dependence of crystallization in implanted polycrystalline silicon films on SiO2. Iverson, R. B.; Reif, R. // Applied Physics Letters;2/22/1988, Vol. 52 Issue 8, p645 

    Crystallization of 1500 Å polycrystalline silicon films self-implanted at doses of 2×1015–6×1015 ions/cm2 is investigated. For doses of 2×1015–5×1015 ions/cm2, crystallization is due to the growth of crystallites which nucleate at a rate which decreases with...

  • Seed selection through ion channeling to modify crystallographic orientations of polycrystalline Si films on SiO2: Implant angle dependence. Kung, K. T-Y.; Iverson, R. B.; Reif, R. // Applied Physics Letters;4/1/1985, Vol. 46 Issue 7, p683 

    Polycrystalline silicon films 4800 Å thick deposited by low pressure chemical vapor deposition at 620 °C on oxidized silicon wafers have been amorphized by implantation with 210-keV Si28 ions to a dose of 1015 cm-2 at 0°, 1°, 3°, 5°, or 7° from normal incidence and...

  • Hall mobility of charge carriers in films of (PbX)1-x(Sm2x3)x semiconductors formed on porous silicon. Hasanov, H. A.; Murguzov, M. I. // Semiconductor Physics, Quantum Electronics & Optoelectronics;2008, Vol. 11 Issue 4, p356 

    Presented paper is devoted to studying the methods to prepare epitaxial films of (PbX)1-x (Sm2X3)x (X - S, Se, Te; x = 0.04) semiconductors and to examine the Hall mobility of charge carriers in these films. It is revealed that the derived dependences �H (T) for the samples on values of the...

  • Time-resolved reflectivity techniques for dynamic studies of electron beam recrystallization of silicon-on-insulator films. Timans, P. J.; McMahon, R. A.; Ahmed, H. // Applied Physics Letters;11/7/1988, Vol. 53 Issue 19, p1844 

    A time-resolved reflectivity (TRR) technique has been developed for dynamic studies of swept beam heating of silicon-on-insulator (SOI) materials. The method exploits the temperature dependence of the reflectivity of SOI films to allow noncontact temperature measurement with high spatial and...

  • Thermally induced defect photoluminescence in hydrogenated amorphous silicon. Gusev, O.; Terukov, E.; Undalov, Yu.; Tsendin, K. // Physics of the Solid State;Feb2011, Vol. 53 Issue 2, p256 

    The intrinsic defect photoluminescence of hydrogenated amorphous silicon ( a-Si:H) films has been investigated at high intensities of optical pumping that lead to heating of the film. It has been revealed that, for short heating times, the intensity of the defect photoluminescence increases...

  • Atomistic simulations of extrinsic defects evolution and transient enhanced diffusion in silicon. Colombeau, B.; Cristiano, F.; Altibelli, A.; Bonafos, C.; Assayag, G. Ben; Claverie, A. // Applied Physics Letters;2/12/2001, Vol. 78 Issue 7, p940 

    In this letter, a physically based model describing the kinetic evolution of extrinsic defects during annealing is presented. The fundamental concepts of Ostwald ripening and formation energy of extrinsic defects are combined in this model, which has been tested against some classical...

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics