TITLE

Elimination of end-of-range and mask edge lateral damage in Ge+ preamorphized, B+ implanted Si

AUTHOR(S)
Ajmera, A. C.; Rozgonyi, G. A.
PUB. DATE
November 1986
SOURCE
Applied Physics Letters;11/10/1986, Vol. 49 Issue 19, p1269
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
The problems of residual extended defects due to end-of-range ion implantation damage and mask edge lateral damage have been solved in this study for shallow boron junctions preamorphized via germanium ion implantation. Defect elimination has been achieved by adjusting the germanium ion energy, dose, and annealing temperature and ambient to minimize the local interstitial point defect concentration and optimize the role of the free surface in defect annihilation. For the combination of shallow, low dose 40 or 60 keV/2×1014 cm-2 Ge+ and 8 keV/1×1015 cm-2 B+ implants, a defect-free structure was obtained following a 1050 °C, 10 s rapid thermal anneal (RTA) in a nonoxidizing Ar ambient. For these samples, boron profiles determined using secondary ion mass spectroscopy (SIMS) showed the junction depth to be approximately 0.17 μm at a background doping of 1×1017 cm-3 with a sheet resistance of 136 Ω/[Laplacian_variant].
ACCESSION #
9821351

 

Related Articles

  • Formation of bubbles in BF+2-implanted silicon. Nieh, C. W.; Chen, L. J. // Applied Physics Letters;6/2/1986, Vol. 48 Issue 22, p1528 

    Fluorine bubbles were observed in 5×1015/cm2 BF+2 -implanted (001) and (111) Si annealed at 1000–1100 °C. Bubbles were found to form in samples annealed at 1100 °C for a time as short as 10 s. The bubbles were distributed mostly near the original amorphous/crystalline interface...

  • Calculation of the fractional interstitial component of boron diffusion and segregation.... Fang, Tilden T.; Fang, Wingra T.C. // Applied Physics Letters;2/5/1996, Vol. 68 Issue 6, p791 

    Calculates the fractional interstitial component of boron diffusion and segregation coeficient in Si[sub 0.8]Ge[sub 0.2]. Use of oxidation-enhanced diffusion; Advantage of the flatness of the final boron profiles; Absence of concentration gradients in the interface.

  • Structure of ([Square_Root]3×[Square_Root]3) R 30°-B at the Si interface studied by grazing incidence x-ray diffraction. Akimoto, Koichi; Hirosawa, Ichiro; Tatsumi, Toru; Hirayama, Hiroyuki; Mizuki, Jun’ichiro; Matsui, Junji // Applied Physics Letters;3/26/1990, Vol. 56 Issue 13, p1225 

    The boron-induced ( 7/8 × 7/8 )R30° reconstruction at the Si interface has been investigated by grazing incidence x-ray diffraction. The in-plane projected struture is found from the structure factors near zero perpendicular momentum transfer. At the a-Si/Si (111) interface, boron atoms...

  • Growth of Si on Si(100) via H/Cl exchange and the effect of interfacial boron. Koleske, D. D.; Gates, S. M.; Beach, D. B. // Journal of Applied Physics;11/1/1992, Vol. 72 Issue 9, p4073 

    Presents a study which had grown silicon on silicon(100) via hydrogen/chlorine exchange and the effect of interfacial boron. Experimental details; Results and discussion; Conclusion.

  • Boron diffusion through thin gate oxides: Influence of nitridation and effect on the Si/SiO2 interface electrical characteristics. Mathiot, D.; Straboni, A.; Andre, E.; Debenest, P. // Journal of Applied Physics;6/15/1993, Vol. 73 Issue 12, p8215 

    Examines the diffusional behavior of boron in SiO[sub2] films. Influence of oxide nitridation on Si/SiO[sub2] interface electrical characteristics; Evolution of the midgap interface state density of a polysilicon gate capacitor; Comparison between calculated and experimental boron profiles.

  • Molecular Functionalization of Planar Nanocrystalline and Porous Nanostructured Diamond to Form an Interface with Newborn and Adult Neurons. Krůšek, Jan; Dittert, Ivan; Smejkalová, Tereza; Kořínek, Miloslav; Gottfriedová, Kristýna; Freislebenová, Hana; Neuhöferová, Eva; Klimša, Ladislav; Sedláková, Silvia; Taylor, Andrew; Mortet, Vincent; Petrák, Václav; Benson, Veronika; Petráková, Vladimíra // Physica Status Solidi (B);Mar2019, Vol. 256 Issue 3, pN.PAG 

    This article examines the ability of newly developed nanostructured porous boron‐doped diamond (BDD) to form an interface with neural cells and the role of molecular functionalization by a polymer on this interface. Due to its high stability, biocompatibility, and electrical properties,...

  • Characterization of boron charge traps at the interface of Si/SiO2 using second harmonic generation. Park, H.; Qi, J.; Xu, Y.; Varga, K.; Weiss, S. M.; Rogers, B. R.; Lüpke, G.; Tolk, N. // Applied Physics Letters;8/10/2009, Vol. 95 Issue 6, p062102 

    We report results from optical second harmonic generation studies of boron charge traps near the interface of Si/SiO2. Our data suggest that a static electric field at the interface is formed during the oxide growth process due to the presence of negative boron ions (B-) in the silicon substrate...

  • Orientation effects in tBN/cBN interfaces: A transmission electron microscopic study. Li, Quan; Bello, I.; Marks, L. D.; Lifshitz, Y.; Lee, S. T. // Applied Physics Letters;1/7/2002, Vol. 80 Issue 1, p46 

    The orientation between cubic boron nitride (cBN) crystallites and the tBN layers on which they grow was studied using high-resolution transmission electron microscopy. BN films were prepared by radio-frequency magnetron sputtering under conditions leading to the formation of ∼100% cBN...

  • Interfacial reaction of BN/Ni3Al. Chou, T. C. // Applied Physics Letters;10/17/1988, Vol. 53 Issue 16, p1500 

    Interfacial reaction between BN and Ni3Al was studied by diffusion bonding at 1000 °C. Error function type diffusion profiles of Ni and Al were observed. Al enrichment at the interface was detected. Kirkendall voids [Trans. Am. Inst. Min. Eng. 171, 130 (1947)] with faceted interfaces were...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics