TITLE

Density measurements, calorimetry, and transmission electron microscopy of icosahedral Mn14Al86

AUTHOR(S)
Kelton, K. F.; Wu, T. W.
PUB. DATE
June 1985
SOURCE
Applied Physics Letters;6/1/1985, Vol. 46 Issue 11, p1059
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
The density and heat of crystallization of rapidly quenched Mn14Al86 were measured and found to be 3.287±0.038 g/cm3 and 16.2 cal/g, respectively. Transmission electron microscopy revealed nodules of the icosahedral phase with lattice fringes. No Kikuchi lines were observed in either selected area or convergent beam diffraction.
ACCESSION #
9817604

 

Related Articles

  • Icosahedral quasicrystal produced by gas evaporation of an Al-Mn alloy. Saito, Yahachi; Chen, Ho S.; Mihama, Kazuhiro // Applied Physics Letters;3/3/1986, Vol. 48 Issue 9, p581 

    Al-Mn alloy particles prepared by evaporation of an Al-10 at. % Mn alloy in He gas have been found to exhibit the same diffraction pattern reported for a melt-spun Al6Mn icosahedral quasicrystal. An x-ray energy dispersive analysis shows a Mn content of about 24 at. %.

  • Interfacial diffusion effect on phase transitions in Al/Mn multilayered thin films. Srivastava, A. K.; Yu-Zhang, K.; Kilian, L.; Frigério, J. M.; Rivory, J. // Journal of Materials Science;Jan2007, Vol. 42 Issue 1, p185 

    Thin films of Al and Mn multilayers were synthesized using thermal evaporation under high vacuum conditions. The whole film thickness containing three bilayers of Al and Mn is about 120 nm. The global concentration of the samples was varied between 10 and 46.5 at.% Mn, by changing the thickness...

  • Twinning and orientation relationships of T-phase precipitates in an Al matrix. Chen, Y.; Yi, D.; Jiang, Y.; Wang, B.; Xu, D.; Li, S. // Journal of Materials Science;Apr2013, Vol. 48 Issue 8, p3225 

    The recent increasing interest of T-phase in Al alloy has been switched to its twins. In this study, we employed high resolution transmission electron microscopy to study and compare the morphology and orientation relationships (OR) of T-phase and its twins in an Al-Cu-Mg-Mn alloy. It is found...

  • Pore formation in aluminum films on macroporous silicon during high-temperature annealing. Zimin, S. P.; Gorlachev, E. S.; Gerke, M. N. // Technical Physics Letters;Feb2008, Vol. 34 Issue 2, p143 

    The surface of an aluminum metallization coating applied on a macroporous silicon layer and annealed for 10–60 min at 550°C has been studied by atomic-force and electron microscopy techniques. It is established that the annealing results in the formation of through (open) macropores...

  • Investigation of the structural transformations in the Al-Li-Cu-Mg (8090) alloy. Gaber, A.; Afify, N. // Applied Physics A: Materials Science & Processing;1997, Vol. 65 Issue 1, p57 

    The precipitation processes in quenched Al-2.4Li-1.16Cu-0.8Mg(wt.%) alloy (8090) from the solid solution state (T[sub q] =803 K) have been investigated via the Vickers microhardness measurements, scanning electron microscopy and differential scanning calorimetry. On the basis of Kissinger�s...

  • Modeling of the Effect of Temperature, Frequency, and Phase Transformations on the Viscoelastic Properties of AA 7075-T6 and AA 2024-T3 Aluminum Alloys. Rojas, Jose; Crespo, Daniel // Metallurgical & Materials Transactions. Part A;Dec2012, Vol. 43 Issue 12, p4633 

    The viscoelastic response of commercial aluminum alloys 7075-T6 and 2024-T3 as a function of temperature is presented. Experimental data are obtained with a dynamic-mechanical analyzer (DMA) at different loading frequencies and compared with the available transmission electron microscopy (TEM)...

  • Transmission electron microscopy and differential scanning calorimetry studies on the precipitation sequence in an Al-Mg-Si alloy: AA6022. Yassar, Reza S.; Field, David P.; Weiland, Hasso // Journal of Materials Research;Oct2005, Vol. 20 Issue 10, p2705 

    The precipitate sequence in a 6022 aluminum alloy was investigated by means of differential scanning calorimetry (DSC), transmission electron microscopy, and Vickers hardness measurements. The solution-treated samples were quenched and then immediately subjected to DSC and isothermal aging...

  • Magnetic nanotubes produced by hydrogen reduction. Sui, Y. C.; Skomski, R.; Sorge, K. D.; Sellmyer, D. J. // Journal of Applied Physics;6/1/2004, Vol. 95 Issue 11, p7151 

    FePt and Fe3O4 nanotubes are produced by hydrogen reduction in nanochannels of porous alumina templates and investigated by electron microscopy, x-ray diffraction, and superconducting quantum interference device magnetometry. Loading the templates with an Fe chloride and Pt chloride mixture,...

  • Martensitic and Magnetic Transformation Behaviors in Heusler-Type NiMnin and NiCoMnin Metamagnetic Shape Memory Alloys. Ito, W.; Imano, Y.; Kainuma, R.; Sutou, Y.; Oikawa, K.; Eshida, K. // Metallurgical & Materials Transactions. Part A;Apr2007, Vol. 38 Issue 4, p759 

    Martensitic and magnetic transformation behaviors of Ni50MnIn, Ni45Co5MnIn, and Ni42.5Co7.5MnIn Heusler alloys were investigated by differential scanning calorimetry (DSC), vibrating sample magnetometry (VSM), and transmission electron microscopy (TEM). The martensitic transformation starting...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics