TITLE

Effect of Surface Treatment with Carbon Dioxide (CO2) Laser on Bond Strength between Cement Resin and Zirconia

AUTHOR(S)
Kasraei, Shahin; Atefat, Mohammad; Beheshti, Maryam; Safavi, Nassimeh; Mojtahedi, Maryam; Rezaei-Soufi, Loghman
PUB. DATE
July 2014
SOURCE
Journal of Lasers in Medical Sciences;Summer2014, Vol. 5 Issue 3, p115
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Introduction: Since it is not possible to form an adequate micromechanical bond between resin cement and zirconia ceramics using common surface treatment techniques, laser pretreatment has been suggested for zirconia ceramic surfaces. The aim of this study was to evaluate the effect of Carbon Dioxide (CO2) Laser treatment on shear bond strength (SBS) of resin cement to zirconia ceramic. Methods: In this in vitro study thirty discs of zirconia with a diameter of 6 mm and a thickness of 2 mm were randomly divided into two groups of 15. In the test group the zirconia disc surfaces were irradiated by CO2 laser with an output power of 3 W and energy density of 265.39 j/cm2. Composite resin discs were fabricated by plastic molds, measuring 3 mm in diameter and 2 mm in thickness and were cemented on zirconia disk surfaces with Panavia F2.0 resin cement (Kuraray Co. Ltd, Osaka, Japan). Shear bond strength was measured by a universal testing machine at a crosshead speed of 0.5 mm/min. The fracture type was assessed under a stereomicroscope at ×40. Surface morphologies of two specimens of the test group were evaluated under SEM before and after laser pretreatment. Data was analyzed by paired t-test (p value < 0.05). Results: The mean SBS values of the laser and control groups were 12.12 ± 3.02 and 5.97 ± 1.14 MPa, respectively. Surface treatment with CO2 laser significantly increased SBS between resin cement and zirconia ceramic (p value = 0.001). Conclusion: Under the limitations of this study, surface treatment with CO2 laser increased the SBS between resin cement and the zirconia ceramic.
ACCESSION #
97769795

 

Related Articles

  • Association of Different Primers and Resin Cements for Adhesive Bonding to Zirconia Ceramics. Akio Maeda, Fernando; Bello-Silva, Marina Stella; de Paula Eduardo, Carlos; Gomes Miranda Junior, Walter; Francisco Cesar, Paulo // Journal of Adhesive Dentistry;2014, Vol. 16 Issue 3, p261 

    Purpose: To evaluate the shear bond strength (SBS) to zirconia ceramics using different associations of primers and resin cements. Materials and Methods: Two blocks of LAVA zirconia (3Y-TZP) were randomly submitted to an application of three different commercially available primers: Alloy Primer...

  • Evaluation of Microshear Bond Strength of Orthodontic Resin Cement to Monolithic Zirconium Oxide as a Function of Surface Conditioning Method. Bavbek, Nehir Canigur; Roulet, Jean-François; Özcan, Mutlu // Journal of Adhesive Dentistry;2014, Vol. 16 Issue 5, p473 

    Purpose: To evaluate the microshear bond strength (μSBS) of orthodontic resin cement to monolithic zirconium oxide ceramic (MZ) after different surface conditioning methods. Materials and Methods: Two types of MZ (BruxZir Solid Zirconia, n = 60; Prettau-Zirkon, n = 60) with two types of...

  • Effect of Surface Treatment and Resin Cement on Microtensile Bond Strength of Zirconia to Dentin. Xiaoli Feng; Ruoyu Liu; Yanli Zhang; Liangjiao Chen; Yaokun Zhang; Longquan Shao // Key Engineering Materials;2014, Vol. 602-603, p602 

    To evaluate the effect of three surface treatments and two resin cements on microtensile bond strength of zirconia to dentin. Sixty human molars were embedded in acrylic resin and sectioned 3 mm below the occlusal plane. Teeth specimens and sixty zirconia specimens were randomized into 3 groups...

  • Influence of Hot-Etching Surface Treatment on Zirconia/Resin Shear Bond Strength. Pin Lv; Xin Yang; Ting Jiang // Materials (1996-1944);Dec2015, Vol. 8 Issue 12, p8087 

    This study was designed to evaluate the effect of hot-etching surface treatment on the shear bond strength between zirconia ceramics and two commercial resin cements. Ceramic cylinders (120 units; length: 2.5 mm; diameter: 4.7 mm) were randomly divided into 12 groups (n = 10) according to...

  • Evaluation of removal forces of implant-supported zirconia copings depending on abutment geometry, luting agent and cleaning method during re-cementation. Rödiger, Matthias; Rinke, Sven; Ehret-Kleinau, Fenja; Pohlmeyer, Franziska; Lange, Katharina; Bürgers, Ralf; Gersdorff, Nikolaus // Journal of Advanced Prosthodontics;Jun2014, Vol. 6 Issue 3, p233 

    PURPOSE. To evaluate the effects of different abutment geometries in combination with varying luting agents and the effectiveness of different cleaning methods (prior to re-cementation) regarding the retentiveness of zirconia copings on implants. MATERIALS AND METHODS. Implants were embedded in...

  • Degree of conversion of two dual-cured resin cements light-irradiated through zirconia ceramic disks. Min-Jeong Kim; Kyo-Han Kim; Young-Kyung Kim; Tae-Yub Kwon // Journal of Advanced Prosthodontics;Nov2013, Vol. 5 Issue 4, p464 

    PURPOSE. The aim of this Fourier transform infrared (FTIR) spectroscopic study was to measure the degree of conversion (DC) of dual-cured resin cements light-irradiated through zirconia ceramic disks with different thicknesses using various light-curing methods. MATERIALS AND METHODS. Zirconia...

  • Spine-Ghost: a new bioactive Cement for Vertebroplasty. VITALE-BROVARONE, Chiara; PONTIROLI, Lucia; NOVAJRA, Giorgia; TCACENCU, Ion; REIS, Joana; MANCA, Antonio // Key Engineering Materials;2014, Vol. 631, p43 

    An innovative, resorbable and injectable composite cement (Spine-Ghost) to be used for augmentation and restoration of fractured vertebrae was developed. Type III a-calcium sulfate hemihydrate (CSH) was selected as the bioresorbable matrix, while spray-dried mesoporous bioactive particles...

  • SEM ANALYSIS OF MORPHOLOGICAL CHANGES ON THE SURFACE OF ZIRCONIA CAUSED BY DIFFERENT SURFACE TREATMENTS. Gašparić, Lana Bergman; Viskić, Joško; Ortolan, Sladana Milardović; Mehulić, Ketij // Acta Stomatologica Croatica;2013, Vol. 47 Issue 4, p366 

    Chipping and delamination of veneering porcelain in zirconia FPDs are described as the most frequent failure reasons. Bond between zirconia core and veneering ceramics in bilayered systems has not yet been clarified. Aim of the study was to explore the level of zirconia surface roughness and its...

  • Sustainable Processing of Cellulose Fiber Cement Composites. Soroushian, Parviz; Jong-Pil Won; Hassan, Maan // ACI Materials Journal;May/Jun2013, Vol. 110 Issue 3, p305 

    The aim of this study was to develop an efficient approach to the processing of cellulose fiber-reinforced cement composites, which makes value-added use of carbon dioxide. Two categories of cellulose fiber cement boards were evaluated: pressed and unpressed. Comparisons were made between the...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics