Studying the Corrosion of Brass Weldments by Weight Losses Method

AUTHOR(S)
Hasan, Aysha
PUB. DATE
May 2014
SOURCE
Australian Journal of Basic & Applied Sciences;May2014, Vol. 8 Issue 7, p106
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Brass is alloys of copper consisting mainly of copper and zinc, and it is welded in the same general manner as copper, but because of the peculiar properties of the alloying metals zinc, it is that must receive certain variation in welding. And because of varial application as structural materials in industries, in this work the general corrosion behavior of 𝛼 – Brass (Cu – 37 Zn) alloy weldments in sulphuric acid and sodium hydroxide solution at room – temperature (298k) were also the microstructure of these weldments before and after corrosion was studied and the specimen 𝛼–Brass (Cu – 37 Zn) alloy were welded by Oxygen – Acetylene mixture with three types of filler rods, 𝛼 – Brass, 𝛼 – 𝛽 -Brass and Tin – brass. The results obtained shows that the acidic media is more aggressive than alkaline media for the three weldments.
ACCESSION #
96583858

 

Related Articles

  • Corrosion behavior of 2024 aluminum alloy anodized in presence of permanganate and phosphate ions. Mohammadi, Maysam; Yazdani, Ali; Bahrololoom, Mohammad; Alfantazi, Akram // Journal of Coatings Technology & Research;Mar2013, Vol. 10 Issue 2, p219 

    In this article, the effects of two inorganic corrosion inhibitors, permanganate and phosphate anions, on morphology, composition, thickness, and corrosion resistance of the anodic film formed on 2024 aluminum alloy in sulfuric acid were investigated. Surface morphology of the oxide films were...

  • The Corrosion Behavior of Ni(Si,Nb) Alloys in Boiling 70 wt.% Sulfuric Acid. Hsu, Jen-Hsien; Larson, Christopher; Newkirk, Joseph; Brow, Richard; Zhang, San-Hong // Journal of Materials Engineering & Performance;Feb2016, Vol. 25 Issue 2, p510 

    Corrosion-resistant Ni(Si,Nb) alloys are promising materials of construction for hydrogen-production systems based on the sulfur-iodine thermochemical cycle. In this work, the corrosion rates of three different Ni(Si,Nb) alloys were measured in boiling 70 wt.% sulfuric acid and a three-stage...

  • WELD CORROSION. Kiser, Samuel D. // Advanced Materials & Processes;Mar2002, Vol. 160 Issue 3, p32 

    Focuses on prevention of weld corrosion. Metal components of welding products; Chemical composition of corrosion-resistant alloys; Equivalence of pitting resistance. INSETS: The Salt River Project at Navajo Station in Page, Arizona;Seminole Electric Co-op in Palatka, Florida.

  • Welding Niobium Alloys. Mertz, James // Welding Journal;Nov2003, Vol. 82 Issue 11, p38 

    Focuses on the characteristics, capabilities and practices for fabrication of niobium alloys. Benefits of using niobium alloys; Sensitivity of niobium alloys to oxidation at high temperature; Susciptibility of niobium to intergranular corrosion at elevated temperature.

  • CLAD ALL OVER.  // MWP;Jul2012, Vol. 156 Issue 5, p68 

    The article focuses on the benefits of weld overlay cladding to protect pipelines from corrosion. It is noted that engineers can specify components in corrosion- or wear-resistant alloys known to withstand the conditions where budget is not a constraint. It is stated that the use of a...

  • THEORETICAL AND EXPERIMENTAL PIECES PLATING ULTRASONIC FIELD. Amza, Gheorghe; Petrescu, Valentin; Apostolescu, Zoia; Teodorescu, Marius Cornel; Dragomir-Groza, Adrian Ioan // Nonconventional Technologies Review / Revista de Tehnologii Neco;Dec2014, Vol. 18 Issue 4, p32 

    This paper presents the importance of the cladding for highly loaded parts from corrosion and / or wear and technologies currently used with advantages and disadvantages. It proposes a new plating technology loaded ultrasonic welding field and establishes the main stages of the technological...

  • Corrosion and Corrosion Inhibition of Aluminum Alloys A5052 and A5754 in Sulfuric Acid Solutions by Some Inorganic Inhibitors. El-Rehim, S. S. Abd; Deyab, M. A.; Hassan, H. H.; El-Moneim, Ahamed Abd // Zeitschrift für Physikalische Chemie;Jun2017, Vol. 231 Issue 6, p1141 

    The corrosion of aluminum alloys (A5052 and 5754) in sulfuric acid solutions was investigated using potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS), scanning electron microscope (SEM), and energy-dispersive X-ray (EDX) methods. For comparison, the corrosion of...

  • Corrosion Behaviour of Alpha Phase Aluminium Bronze Alloy in Selected Environments. BALOGUN, Oluwayomi; BORODE, Joseph; ALANEME, Kenneth; BODUNRIN, Michael // Leonardo Electronic Journal of Practices & Technologies;Jan/Jun2014, Issue 24, p113 

    This research investigated the corrosion behaviour of aluminium (8 wt %) bronze alloys produced via sand casting in acidic, alkaline, and marine environments. The aluminium bronze was produced from aluminium (6063) alloy and copper scraps by sand casting according to European standard...

  • Corrosion and Corrosion Inhibition of High Strength Low Alloy Steel in 2.0M Sulfuric Acid Solutions by 3-Amino-1,2,3-triazole as a Corrosion Inhibitor. Sherif, El-Sayed M.; Abbas, Adel Taha; Gopi, D.; El-Shamy, A. M. // Journal of Chemistry;2014, p1 

    The corrosion and corrosion inhibition of high strength low alloy (HSLA) steel after 10 min and 60 min immersion in 2.0M H2SO4 solution by 3-amino-1,2,4-triazole (ATA) were reported. Several electrochemical techniques along with scanning electron microscopy (SEM) and energy dispersive X-ray...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics