Synthesis of a Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub y] high-temperature superconducting phase with T[sub c][sup °] above 100 K

Tomilo, Zh. M.; Prytkova, N. A.; Gololobov, E. M.; Turtsevich, D. M.
June 1997
Technical Physics Letters;Jun97, Vol. 23 Issue 6, p422
Academic Journal
A high-temperature superconductor with the Bi[sub 2]Sr[sub 2]CaCu[sub 2]O[sub y] structure and a superconducting transition temperature T[sup º, sub c] = 102-107 K has been synthesized. The synthesis conditions are described and results of a phase analysis, and of resistive and inductive measurements are reported.


Related Articles

  • Angle-dependent laser-induced voltages in room-temperature polycrystalline wafers of YBa2Cu3O7-x. Tate, K. L.; Hilinski, E. F.; Foster, S. C. // Applied Physics Letters;12/3/1990, Vol. 57 Issue 23, p2407 

    Room-temperature laser-induced voltages were observed in unsupported, polycrystalline wafers of YBa2Cu3O7-x in the absence of a transport current. Peak voltages of ∼1 V were detected in response to 40 mJ pulses of 532 nm light. The rise and fall times for the signals were detector limited....

  • Single-crystal preparation and some characterizations of the superconducting Y-Ba-Cu oxide. Haneda, Hajime; Isobe, Mitsumasa; Hishita, Shunichi; Ishizawa, Yoshio; Shirasaki, Shin-ichi; Yamamoto, Taisei; Yanagitani, Takagimi // Applied Physics Letters;11/30/1987, Vol. 51 Issue 22, p1848 

    Single crystals of Ba2YCu3O7-δ were prepared from melts of a BaO-Y2O3-CuO mixture and characterized by the x-ray microprobe analyzer and x-ray diffraction. Electrical resistivity was measured by the standard four-terminal method. Some crystals have the critical temperature above 77 K. After...

  • Structural characterization of a TlCaBaCu oxide in Tc onset=155 K and Tc zero=123 K superconducting specimens. Liang, J. M.; Liu, R. S.; Chang, L.; Wu, P. T.; Chen, L. J. // Applied Physics Letters;10/10/1988, Vol. 53 Issue 15, p1434 

    The crystal structure of a Tl-Ca-Ba-Cu-O compound in Tc onset=155 K and Tc zero=123 K superconducting specimens was characterized by transmission electron microscopy. Convergent beam electron diffraction analysis established that the phase is of P4/mcc space group. The lattice parameters of the...

  • Properties of Bi(Pb)-Sr-Ca-Cu-O superconducting tapes prepared by the doctor-blade process. Yanagisawa, E.; Morimoto, T.; Dietderich, D. R.; Kumakura, H.; Togano, K.; Maeda, H. // Applied Physics Letters;6/19/1989, Vol. 54 Issue 25, p2602 

    Improved superconducting and mechanical properties were obtained for Bi(Pb)-Sr-Ca-Cu-O tapes, prepared by the combined process of doctor-blade casting, cold rolling, and sintering. The tape has an oriented microstructure with the high Tc plate-like grains having their c axes perpendicular to the...

  • Effect of Li doping on the critical temperature and glass formation in the Bi–Sr–Ca–Cu–O system. Volkov, M. P.; Melekh, B. T.; Bakharev, V. I.; Kartenko, N. F.; Matykin, N. V.; Filin, Yu. N. // Physics of the Solid State;Jan99, Vol. 41 Issue 1, p15 

    A study has been made of the glass-forming ability, structure, and superconducting properties of Bi[sub 2.2]Sr[sub 1.8]Ca[sub 1.05]Cu[sub 2.15]Li[sub x]O[sub y] and Bi[sub 2.2]Sr[sub 1.8]Ca[sub 1.05]Cu[sub 2.15 - x]Li[sub x]O[sub y] (x = 0; 0.3; 0.5; 0.7). The compounds were melted by rf at T =...

  • Vapor-deposited superconducting YBa2Cu3O7-δ lines: Effect of thickness and width on morphology. Phillips, J. R.; Mayer, J. W.; Martin, J. A.; Nastasi, M. // Applied Physics Letters;4/2/1990, Vol. 56 Issue 14, p1374 

    Lines of different widths and thicknesses of YBa2Cu3O7-δ were prepared on SrTiO3 and compared for signs of morphological dependence on line dimensions. The lines were prepared on (100) SrTiO3 by electron beam (e-beam) coevaporation, e-beam resist lift-off, and annealing in oxygen to 850...

  • Tailored thin films of a superconducting Bi-Sr-Ca-Cu oxide prepared by incorporation of exotic atoms—control of the distance between CuO2 layers. Tabata, Hitoshi; Murata, Osamu; Kawai, Tomoji; Kawai, Shichio // Applied Physics Letters;4/16/1990, Vol. 56 Issue 16, p1576 

    A layer-by-layer successive deposition method utilizing laser ablation has been applied to the site-selective incorporation of +1, +2, and +3 ions at the Ca and Sr site of Bi2Sr2Ca1Cu2O8 superconducting films. The replacement of Ca by larger ions increases the lattice parameter c and Tc...

  • Giant microwave losses in a YBaCuO bicrystal. Pakulis, E. J.; Blum, S. E. // Applied Physics Letters;10/1/1990, Vol. 57 Issue 14, p1464 

    We have observed a large peak in microwave losses, as a function of temperature, in a superconducting Y1Ba2Cu3O7 bicrystal containing a large-area, low-angle grain boundary. The maximum observed loss was approximately twice the normal state loss. We attribute the peak to enhanced losses...

  • Tl2Ca1Ba2Cu2O8+x high Tc superconductors processed by the sol-gel technique. Kordas, G.; Teepe, M. R. // Applied Physics Letters;10/1/1990, Vol. 57 Issue 14, p1461 

    Tl2Ca1Ba2Cu2O8+x high Tc superconductors were developed using a new alkoxide sol-gel system. Barium-, calcium-, thallium-methoxyethoxide and Cu(II) ethoxide precursors were used for the formation of homogeneous sols. Solubility of the Cu(II) ethoxide was aided by using a 2-methoxyethanol/methyl...


Read the Article


Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics