TITLE

Microwave surface resistance of MgB[sub 2]

AUTHOR(S)
Zhukov, A. A.; Purnell, A.; Miyoshi, Y.; Bugoslavsky, Y.; Lockman, Z.; Berenov, A.; Zhai, H. Y.; Christen, H. M.; Paranthaman, M. P.; Lowndes, D. H.; Jo, M. H.; Blamire, M. G.; Hao, Ling; Gallop, J.; MacManus-Driscoll, J. L.; Cohen, L. F.
PUB. DATE
April 2002
SOURCE
Applied Physics Letters;4/1/2002, Vol. 80 Issue 13, p2347
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
The microwave power and frequency dependence of the surface resistance of MgB[sub 2] films and powder samples were studied. Sample quality is relatively easy to identify by the breakdown in the ω² law for poor-quality samples at all temperatures. The performance of MgB[sub 2] at 10 GHz and 21 K was compared directly with that of high-quality YBCO films. The surface resistance of MgB[sub 2] was found to be approximately three times higher at low microwave power and showed an onset of nonlinearity at microwave surface fields ten times lower than the YBCO film. It is clear that MgB[sub 2] films are not yet optimized for microwave applications.
ACCESSION #
6391205

 

Related Articles

  • Magnetic and electric "dead" layers in (La0.7Sr0.3)MnO3 thin films. Borges, R. P.; Guichard, W.; Lunney, J. G.; Coey, J. M. D.; Ott, F. // Journal of Applied Physics;4/1/2001, Vol. 89 Issue 7 

    The magnetic, transport, and structural properties of (La[sub 0.1]Sr[sub 0.3])MnO[sub 3] films deposited on MgO (001) are reported as a function of thickness and substrate temperature. The substrate temperature is fundamental in determining the structural properties and a deviation from the...

  • Correlation of power handling capability and intermodulation distortion in YBa[sub 2]Cu[sub 3]O[sub 7-δ] thin films. Lahl, P.; Wo¨rdenweber, R.; Hein, M. // Applied Physics Letters;7/23/2001, Vol. 79 Issue 4 

    The nonlinearity of the microwave properties of coplanar thin-film YBa[sub 2]Cu[sub 3]O[sub 7-δ] resonators are examined by measurements of the degradation of the quality factor Q[sub L] and the increase of the two-tone third-order intermodulation distortion signal with increasing microwave...

  • Josephson effects in YBa[sub 2]Cu[sub 3]O[sub y] grain boundary junctions on (100)MgO bicrystal.... Kiejin Lee; Iguchi, Ienari // Applied Physics Letters;2/6/1995, Vol. 66 Issue 6, p769 

    Investigates the Josephson effect in artificial grain-boundary junction on (100)Magnesium oxide bicrystal substrates. Details on in-plane orientations observed at junction interface; Information on the receiver frequencies with maximum Josephson effect; Feasibility of the bicrystals as...

  • Structure and superconducting properties of sputtered Gd-Ba-Cu-O thin films. Kamada, Takeshi; Setsune, Kentaro; Hirao, Takashi; Wasa, Kiyotaka // Applied Physics Letters;5/16/1988, Vol. 52 Issue 20, p1726 

    Superconducting Gd-Ba-Cu-O thin films were deposited on MgO substrates by rf magnetron sputtering. Preparation temperature dependence on the crystallization behavior and on the superconductive properties of this film have been investigated in correlation with the target-substrate spacing. A...

  • New 100 K TlSr[sub 2](Ca,Cr)Cu[sub 2]O[sub 7] superconducting films. Tang, Y.Q.; Sheng, Z.Z. // Applied Physics Letters;6/15/1992, Vol. 60 Issue 24, p3057 

    Reports the preparation and characterization of TlSr[sub 2](Ca,Cr)Cu[sub 2]O[sub 7] superconducting thin films on magnesium oxide(100) substrates. Deposition of films via spray pyrolysis and thallium diffusion; Application of a Sloan Dektak surface profilemeter to measure film thickness;...

  • Electrical properties of MgO insulating layers in spin-dependent tunneling junctions using Fe[sub3]O[sub4]. Kiyomura, T.; Maruo, Y.; Gomi, M. // Journal of Applied Physics;10/15/2000, Vol. 88 Issue 8, p4768 

    Investigates the growth conditions and electrical properties MgO epitaxial thin films, which have potential applications as insulating layers for spin-dependent tunneling devices where Fe[sub 3]O[sub 4] as one of the magnetic electrodes. Growing of epitaxial MgO films with high crystalline...

  • Preparation of epitaxial Pb(ZrxTi1-x)O3 thin films and their crystallographic, pyroelectric, and ferroelectric properties. Takayama, Ryoichi; Tomita, Yoshihiro // Journal of Applied Physics;2/15/1989, Vol. 65 Issue 4, p1666 

    Presents a study in which epitaxial lead zirconate-titanate (PZT) thin films with the tetragonal and rhombohedral structures were obtained MgO single crystals and epitaxial platinum films. Properties of thin films; Composition of the films; Pyroelectric currents detected on PZT films.

  • Preferred orientation effects in coevaporated films of DyBa2Cu3O7-x superconductors. Budhani, R. C.; Xu, Youwen; Wiesmann, H.; Ruckman, M. W.; Sabatini, R. L. // Journal of Applied Physics;11/15/1989, Vol. 66 Issue 10, p4896 

    Deals with a study which investigated the effect of thermal coevaporation on deposit superconducting thin films on magnesium oxide substrates. Information on superconducting thin films; Methodology of the study; Results and discussion.

  • Magnetic properties of Co/MgO multilayered films. Nishikawa, Masakazu; Kita, Eiji; Erata, Tomoki; Tasaki, Akira // Journal of Applied Physics;5/15/1993, Vol. 73 Issue 10, p6350 

    Presents a study which fabricated multilayered thin films composed of cobalt (Co) and MgO layers with an ultrahigh vacuum deposition technique. Film structures; Magnetization measurements; Angle x-ray scattering patterns for Co/MgO multilayered thin films.

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics