TITLE

Orientation-controlled nonepitaxial L1[sub 0] CoPt and FePt films

AUTHOR(S)
Zeng, H.; Yan, M. L.; Powers, N.; Sellmyer, D. J.
PUB. DATE
April 2002
SOURCE
Applied Physics Letters;4/1/2002, Vol. 80 Issue 13, p2350
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
We report results on highly oriented, face-centered tetragonal ordered CoPt and FePt thin films grown nonepitaxially by directly depositing films on thermally oxidized Si substrates and subsequent annealing. By controlling the thickness, composition, and annealing conditions, and/or depositing a proper underlayer, nearly perfect (001)-oriented CoPt and FePt films can be obtained. Magnetic measurements reveal large perpendicular anisotropy for such films.
ACCESSION #
6391204

 

Related Articles

  • Connecting disorder and magnetic properties in CoFe thin films. Freeland, J. W.; Freeland, J.W.; Bussmann, K.; Bussman, K.; Idzerda, Y. U.; Idzerda, Y.U. // Applied Physics Letters;5/1/2000, Vol. 76 Issue 18 

    Through a direct study of the chemical and magnetic interfacial disorder in conjunction with magnetic property measurements, evidence is presented that the grain size is the ultimate factor in determining the magnetic coercivity in CoFe thin film structures. © 2000 American Institute of Physics.

  • Compositional dependence of Young's moduli for amorphous FeCo-SiO2 thin films. Zhang, L.; Guo, Q.; Zhu, Z. W.; Bi, L.; Xie, J. L.; Deng, L. J. // Journal of Applied Physics;Apr2011, Vol. 109 Issue 7, p07A929 

    Systematic force-deflection measurements with microcantilevers and a combinatorial-deposition method have been used to investigate the Young's moduli of amorphous composite FeCo-SiO2 thin films as a function of film composition, with high compositional resolution. It is found that the modulus...

  • Magnetic properties of ultrathin Co/Ag/Pt(111) films. Su, C. W.; Tzeng, C.L.; Ho, H.Y.; Sherna, C.S. // Journal of Applied Physics;11/1/2003, Vol. 94 Issue 9, p5873 

    The magnetic properties of Co on Pt(111) with 1 ML Ag buffer layer were studied by magneto-optical Kerr effect. The easy axis of the magnetization of Co deposited on 1 ML Ag/Pt(111) switches from the out-of-plane to the in-plane direction when the coverage of Co is larger than 1 ML. The easy...

  • Compositional dependence of magnetic properties of Co–Pt thin films. Pandey, K. K. Mani; Chen, J. S.; Chow, G. M. // Journal of Applied Physics;9/1/2006, Vol. 100 Issue 5, p054909 

    The effects of Pt concentrations on the magnetic properties of Co100-xPtx (0<=x at. %<=43) films deposited on Ru underlayer were investigated. The Co72Pt28 film sputter deposited at room temperature showed out-of-plane coercivity of 5.5 kOe, unit remanent squareness (Mr/Ms=1), and uniaxial...

  • Spin-orbit enhanced demagnetization rate in Co/Pt-multilayers. Kuiper, K. C.; Roth, T.; Schellekens, A. J.; Schmitt, O.; Koopmans, B.; Cinchetti, M.; Aeschlimann, M. // Applied Physics Letters;11/17/2014, Vol. 105 Issue 20, p1 

    In order to explore the role of enhanced spin-orbit interactions on the laser-induced ultrafast magnetization dynamics, we performed a comparative study on cobalt thin films and Co/Pt multilayers. We show that the presence of the Co/Pt interfaces gives rise to a three-fold faster demagnetization...

  • Fabrication and magnetic properties of Fe/Pt multilayered nanowires. Wang, Huixin; Wu, Yu Cheng; Zhang, Lide; Hu, Xiaoye // Applied Physics Letters;12/4/2006, Vol. 89 Issue 23, p232508 

    Fe/Pt multilayered nanowires with well-defined interfaces and layer thicknesses were fabricated by a pulse-plating technique in nanoporous anodic alumina templates. The structure, surface morphology, and magnetic properties of the multilayered nanowire arrays have been characterized by x-ray...

  • Morphology and domain pattern of L1[sub 0] ordered FePt films. Li, G.O.; Takahoshi, H.; Ito, H.; Saito, H.; Ishio, S.; Shima, T.; Takanashi, K. // Journal of Applied Physics;11/1/2003, Vol. 94 Issue 9, p5672 

    Magnetic force microscope (MFM) was used to characterize the L1[sub 0] ordered FePt(001) films sputter deposited directly on MgO(001) substrates at an elevated temperature. With the change of nominal thickness (t[sub N]), the morphology varied from isolated particles to continuous films. The...

  • Crystallography ordering studies of the L10 phase transformation of FePt thin film with Ag top layer. Zhao, Z. L.; Inaba, K.; Ito, Y.; Chen, J. S.; Liu, B. H.; Ding, J.; Wang, J. P. // Journal of Applied Physics;6/1/2004, Vol. 95 Issue 11, p7154 

    Ag has been intensively studied to improve the phase transformation of the L10 FePt. The magnetic properties of the FePt thin films with ultrathin Ag top layers prepared by magnetron sputtering have been studied. The crystallopgraphic ordering of the L10 FePt is significantly promoted with Ag...

  • Transmission electron microscopy study of CoFe films with high saturation magnetization. Craig, B. R.; McVitie, S.; Chapman, J. N.; Johnston, A. B.; O’Donnell, D. O. // Journal of Applied Physics;9/1/2006, Vol. 100 Issue 5, p053915 

    Transmission electron microscopy (TEM) has been used to study magnetization processes in four high moment CoFe films. While all films were of similar total thickness, 50 nm, the differences between them were the inclusion or otherwise of a seed layer and the introduction of nonmagnetic spacers...

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics