Emission zone in organic light-emitting devices having a single layer of polyphenylenevinylene derivatives

Matsumura, Michio; Manabe, Kaoru
December 2001
Applied Physics Letters;12/31/2001, Vol. 79 Issue 27, p4491
Academic Journal
Light-emitting properties of devices fabricated from a copolymer of p-phenylenevinylene derivatives, 98% 3-[4′-(3,7-dimethyloctyloxy)phenylene]-p-phenylenevinylene and 2% 2-methoxy-5-(2-ethylhexyloxy)-p-phenylenevinylene (MEH–PV), were investigated. The emission efficiency of the devices showed strong oscillatory dependence on the film thickness, and the frequency agreed with that expected from a localized emission near the indium–tin–oxide (ITO) electrode. Although holes are injected from the ITO electrode into the copolymer layer, they are probably trapped by the MEH–PV unit of the copolymer. On the other hand, electrons are easily transported through the copolymer layer. These are probably the reasons for the confinement of the light-emitting zone near the ITO/copolymer interface. The confined light-emitting zone leads to high emission. For comparison, the properties of devices based on a homopolymer were examined. In this case, the emission zone was distributed over a wide region, and the light-emission efficiency was low. © 2001 American Institute of Physics.


Related Articles

  • Schott Fostec unveils universal light.  // Business Journal (Central New York);2/21/2003, Vol. 17 Issue 8, p18 

    Reports on the development of a Universal Light Source using DC power by Schott Fostec in New York.

  • Static space charge in evaporated ZnS:Mn alternating-current thin-film electroluminescent devices. Hitt, J. C.; Keir, P. D.; Wager, J. F.; Sun, S. S. // Journal of Applied Physics;1/15/1998, Vol. 83 Issue 2, p1141 

    Presents a study on the static space charge in evaporated ZnS. details on the alternating-current thin film electroluminescent devices. Information on the presence of the positive space charge; Methodology used to obtain results of voltage pulse; Information on the differentiation of external...

  • Semiconductors.  // Electronic News;1/6/97, Vol. 43 Issue 2149, p16 

    Presents a diagram of Planar America's RGB color active matrix electroluminescent (AMEL) structure. Low-power, light weight and emissive characteristics; Thin-film single-crystal silicon-on-insulator wafers.

  • Doping effects in organic electroluminescent devices. Yang, Jie; Shen, Jun // Journal of Applied Physics;8/15/1998, Vol. 84 Issue 4, p2105 

    Focuses on the study of several doping effects in organic electroluminescent devices, within a framework of the trap-charge limited conduction models. Information on the conductivity of the organic materials; Reference to the complete energy and charge profiles; Proposal of an experimental...

  • How does the Timex Indiglo nightlight work? Wessner, Cecelia // Popular Science;Feb96, Vol. 248 Issue 2, p78 

    Reports on the functioning of the electroluminescent dial in the Timex's Indiglo watches.

  • Improved drive voltages of organic electroluminescent devices with an efficient p-type aromatic diamine hole-injection layer. Ganzorig, Chimed; Fujihira, Masamichi // Applied Physics Letters;12/18/2000, Vol. 77 Issue 25 

    An SbCl[sub 5]-doped N,N′-diphenyl-N,N′-bis(3-methylphenyl)-1,1′-biphenyl-4,4′-diamine (TPD) thin film was studied as a hole-injection layer in low-molecular-weight organic electroluminescent (EL) devices. EL characteristics of devices with a TPD hole-injection layer...

  • Observation of double light pulses in thin-film ZnS:Mn electroluminescent devices. Bringuier, E.; Geoffroy, A. // Applied Physics Letters;6/30/1986, Vol. 48 Issue 26, p1780 

    Thin-film ZnS:Mn electroluminescent devices can exhibit, under pulsed electrical excitation, a double light pulse, as has been previously observed in other phosphors. We specify the conditions under which this phenomenon appears and relate it to the basic mechanism of carrier emission in the...

  • Mechanism of electroluminescence in alkaline-earth sulfides. Crandall, Richard S. // Applied Physics Letters;3/9/1987, Vol. 50 Issue 10, p551 

    A novel use of a staircase voltage waveform shows that three light emission peaks can be produced with a unipolarity voltage pulse in alkaline-earth-sulfide electroluminescent devices. Two peaks following the voltage decrease demonstrate the following: Light can be produced at fields much below...

  • Electroluminescent lamps: Sharp answers to flat lighting. Schweher, Bill // EDN;02/18/99, Vol. 44 Issue 4, p48 

    Describes how electroluminescent lamps work. Use of electroluminescent lamps as backlighting for liquid crystal displays in pagers, cell phones, watches and control panels; Lighting sources for safety strips and highlighting; Even illumination of a flat area; History of electroluminescent...

  • Demonstration of cascade process in InAs/GaInSb/AlSb mid-infrared light emitting devices. Dupont, E.; McCaffrey, J. P.; Liu, H. C.; Buchanan, M.; Yang, Rui Q.; Lin, C.-H.; Zhang, D.; Pei, S. S. // Applied Physics Letters;3/23/1998, Vol. 72 Issue 12 

    We demonstrate the cascade process in mid-infrared electroluminescent InAs/GaInSb/AlSb multi-quantum-well devices. We report the proportional relation between the emitted optical power and the number of periods. This observed scaling is associated with the sequential transport of electrons from...


Read the Article


Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics