TITLE

Magnetic anisotropies in Ni–Mn–Ga films on MgO(001) substrates

AUTHOR(S)
Chernenko, V. A.; Golub, V.; Barandiarán, J. M.; Salyuk, O. Y.; Albertini, F.; Righi, L.; Fabbrici, S.; Ohtsuka, M.
PUB. DATE
January 2010
SOURCE
Applied Physics Letters;1/25/2010, Vol. 96 Issue 4, p042502
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Ferromagnetic resonance was used to study the influence of temperature and film thickness on magnetic properties of Ni–Mn–Ga films deposited on single crystal MgO(001) substrates. It has been shown that depending on the film thickness and preparation condition, three configurations of magnetic anisotropy can be realized in these films. The temperature dependence of the anisotropy field is determined.
ACCESSION #
47807487

 

Related Articles

  • A theoretical investigation of the effect of the oblique anisotropy axis on the ferromagnetic... Layadi, A. // Journal of Applied Physics;8/1/1999, Vol. 86 Issue 3, p1625 

    Presents information on a study which investigated the effect of the oblique anisotropy axis on the ferromagnetic resonance linewidth of a thin film. General formula for mode linewidth; Research design and methodology; Conclusions.

  • Alternating current-excited magnetoresistive sensor. Ripka, P. // Journal of Applied Physics;4/15/1996, Vol. 79 Issue 8, p5211 

    Discusses a study which measured the magnetic field in thin film anisotropic magnetoresistors. Disadvantage of permalloy magnetoresistors; Results and discussion.

  • Structural, static and dynamic magnetic properties of Co2MnGe thin films on a sapphire a-plane substrate. Belmeguenai, M.; Zighem, F.; Chauveau, T.; Faurie, D.; Roussigné, Y.; Chérif, S. M.; Moch, P.; Westerholt, K.; Monod, P. // Journal of Applied Physics;Oct2010, Vol. 108 Issue 6, p063926 

    Magnetic properties of Co2MnGe thin films of different thicknesses (13, 34, 55, 83, 100, and 200 nm), grown by rf sputtering at 400 °C on single crystal sapphire substrates, were studied using vibrating sample magnetometry and conventional or microstrip line ferromagnetic resonance. Their...

  • Substrate effect on the magnetic behavior of manganite films. Steren, L. B.; Sirena, M.; Guimpel, J. // Journal of Applied Physics;5/1/2000, Vol. 87 Issue 9, p6755 

    The film thickness (t) dependence of the magnetic properties of La[sub 0.6]Sr[sub 0.4]MnO[sub 3] (LSMO) films grown on (001) MgO and (001) SrTiO[sub 3] substrates has been studied. Hysteresis loops measured at low temperature show a smooth increase of the retentivity accompanied by a decrease of...

  • Soft-magnetic properties of Fe–Co–B thin films for ultra-high-frequency applications. Chen, L. H.; Klemmer, T. J.; Ellis, K. A.; van Dover, R. B.; Jin, S. // Journal of Applied Physics;5/1/2000, Vol. 87 Issue 9, p5858 

    Fe[sub 67]Co[sub 18]B[sub 15] amorphous thin films were sputter deposited on glass substrates under a uniform applied magnetic field. The films exhibit excellent soft-magnetic properties of 4πM[sub s]∼17.5 kG, H[sub c]∼0.3 Oe, and H[sub k] (anisotropy field) ∼22 Oe. The...

  • Direct observation of magnetization reversal and low field magnetoresistance of epitaxial La0.7Sr0.3MnO3/SrTiO3 (001) thin films at room temperature. Fadil, D.; Wu, S.; Perna, P.; Renault, B.; Saïb, M.; Lebargy, S.; Gasnier, J.; Guillet, B.; Routoure, J.-M.; Flament, S.; Méchin, L. // Journal of Applied Physics;Jul2012, Vol. 112 Issue 1, p013906 

    We have observed the in-plane magnetic domain arrangement during magnetization reversal in a 40 nm thick La0.7Sr0.3MnO3/SrTiO3 (001) thin film patterned into 500 μm long microbridges of width 50 or 100 μm. Magneto-optical Kerr effect microscopy was used at room temperature and magnetic...

  • Characteristic field angular dependence of magnetization switching assisted by spin wave excitation. Seki, Takeshi; Hotta, Kyoko; Imamura, Hiroshi; Nozaki, Yukio; Takanashi, Koki // Applied Physics Letters;9/16/2013, Vol. 103 Issue 12, p122403 

    We found the characteristic dependence of magnetization switching assisted by spin wave excitation on the magnetic field angle (θ) for exchange-coupled L10-FePt/Permalloy bilayers, where θ was the angle from the easy magnetization axis of L10-FePt. Without the spin wave being excited, an...

  • Transformation volume effect on the magnetic anisotropy of Ni-Mn-Ga thin films. L'vov, V. A.; Golub, V.; Salyuk, O.; Barandiarán, J. M.; Chernenko, V. A. // Journal of Applied Physics;1/21/2015, Vol. 117 Issue 3, p033901-1 

    Ni-Mn-Ga ferromagnetic shape memory films with similar thickness and chemical composition, deposited onto cold (with a subsequent annealing) and hot MgO(001) substrates exhibit different internal stress and structure giving rise to a different orientation of the magnetic easy axes. A...

  • Tunable microwave magnetic properties in oblique deposited CoHf/Ta multilayers. Guozhi Chai; Xinhua Wang; Zhiling Wang; Desheng Xue // Journal of Applied Physics;2015, Vol. 117 Issue 6, p063901-1 

    In this work, the microwave magnetic properties of oblique deposited CoHf/Ta multilayers were investigated. The high frequency magnetic properties of CoHf/Ta multilayers showed different behaviors with oblique angle for different Ta interlayer thickness t. For example, when the Ta interlayer...

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics