Meyer-Neldel rule in amorphous strontium titanate thin films

AUTHOR(S)
Morii, K.; Matsui, T.; Tsuda, H.; Mabuchi, H.
PUB. DATE
October 2000
SOURCE
Applied Physics Letters;10/9/2000, Vol. 77 Issue 15
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
In this letter, we report the experimental result indicating that the electrical conductivity in thin films of amorphous strontium titanate (a-STO) is well fit to the Meyer-Neldel (MN) rule over the temperature range 300-470 K. The films were ion-beam sputtered and annealed in two different atmospheres: a vacuum and flowing oxygen. The MN plots for the films show two parallel straight lines depending on the annealing atmosphere, which give the identical MN parameters of about 35 meV with the conductivity prefactors of 9.3x10[sup -10] and 2.3x10[sup -14](Ω cm)[sup -1] for the vacuum- and oxygen- annealed films, respectively. © 2000 American Institute of Physics.
ACCESSION #
4413441

 

Related Articles

  • Electrical conductivity of sputtered films of strontium titanate. Gerblinger, Josef; Meixner, Hans // Journal of Applied Physics;6/15/1990, Vol. 67 Issue 12, p7453 

    Studies the electrical conductivity of sputtered thin films of strontium titanate. Previous studies on the electrical conductivity of strontium titanate; Preparation of the thin films; Properties of the sputtered films.

  • Effects of ambient gas pressure on (1-x) SrTiO3-xBaTiO3 films prepared by pulsed laser deposition. Tseng, Tzu-Feng; Yeh, Ming-Hua; Liu, Kuo-Shung; Lin, I-Nan // Journal of Applied Physics;11/1/1996, Vol. 80 Issue 9, p4984 

    Deals with a study which assessed the effect of ambient gas pressure in pulsed laser deposition on the lattice parameters of strontium barium titanate thin films. Experimental details; Results; Discussion; Conclusion.

  • High tunability of lead strontium titanate thin films using a conductive LaNiO3 as electrodes. Jain, M.; Karan, N. K.; Yoon, J.; Wang, H.; Usov, I.; Katiyar, R. S.; Bhalla, A. S.; Jia, Q. X. // Applied Physics Letters;8/13/2007, Vol. 91 Issue 7, p072908 

    Highly tunable films of dielectric PbxSr1-xTiO3 (with x=0.3 and 0.4) have been deposited on conductive LaNiO3 coated LaAlO3 substrates using a sol-gel technique. The processing condition was found to greatly influence the microstructure as well as the dielectric and electrical properties of the...

  • Electrical and optical properties of strongly reduced epitaxial BaTiO[sub 3-x] thin films. Zhao, Tong; Tong Zhao; Chen, Zheng-Hao; Zheng-Hao Chen; Chen, Fan; Fan Chen; Lu, Hui-Bin; Hui-Bin Lu; Yang, Guo-Zhen; Guo-Zhen Yang; Cheng, Huan-Sheng; Huan-Sheng Cheng // Applied Physics Letters;12/25/2000, Vol. 77 Issue 26 

    A series of BaTiO[sub 3-x] (x=0, 0.07, 0.18, and 0.48) thin films with c-axis oriented tetragonal perovskite structures were epitaxially grown on SrTiO[sub 3] (100) and MgO (100) substrates by laser molecular-beam epitaxy under various oxygen pressures. The electrical conductivity of the...

  • Superconductivity in La-doped strontium titanate thin films. Olaya, David; Feng Pan; Rogers, Charles T.; Price, Jonn C. // Applied Physics Letters;5/17/2004, Vol. 84 Issue 20, p4020 

    We report on the superconductivity of lanthanum-doped SrTiO3 thin films grown by off-axis laser ablation on LaAlO3, SrTiO3, and NdGaO3 substrates in oxygen partial pressures ranging from 10-8 T to 21 mTorr. The La/Sr doping ratio of the ablation target was 1%. The resulting films have carrier...

  • Conductivity enhancement of ultrathin LaNiO3 films in superlattices. Son, Junwoo; LeBeau, James M.; Allen, S. James; Stemmer, Susanne // Applied Physics Letters;11/15/2010, Vol. 97 Issue 20, p202109 

    The resistance of superlattices composed of bilayers of ultrathin (∼4 unit cells) of LaNiO3 and ∼3 unit cells of insulating SrTiO3 is explored as a function of temperature and the number of bilayers. All superlattices with more than one bilayer are metallic, whereas a single bilayer is...

  • The optical and electronic transport properties of SrSn0.95Fe0.05O3 films. Prathiba, G.; Venkatesh, S.; Kumar, N. Harish // AIP Conference Proceedings;6/5/2012, Vol. 1447 Issue 1, p1219 

    SrSn0.95Fe0.05O3 films were grown on oxidized silicon and quartz substrates by RF sputtering technique. The electronic transport and optical properties of the films were investigated. The temperature dependence of electronic conductivity has been analyzed quantitatively using Mott's small...

  • Highly aligned, spin polarized thin films of Sr[sub 2]FeMoO[sub 6] by a chemical vapor process. Rager, J.; Berenov, A. V.; Cohen, L. F.; Branford, W. R.; Bugoslavsky, Y. V.; Miyoshi, Y.; Ardakani, M.; MacManus-Driscoll, J. L. // Applied Physics Letters;12/23/2002, Vol. 81 Issue 26, p5003 

    Highly oriented films of Sr[sub 2]FeMoO[sub 6] were fabricated by ultrasonic spray pyrolysis. A combined organic/inorganic solution was developed and the films were deposited on single-crystal LaA1O[sub 3] between 600°C and 900°C followed by postannealing at 850°C or 1200°C in Ar/5%...

  • On the effect of hydrogen incorporation in strontium titanate layers grown by high vacuum... Schneider, Jochen M.; Hjorvarsson, Bjorgvin // Applied Physics Letters;11/29/1999, Vol. 75 Issue 22, p3476 

    Studies the effect of hydrogen incorporation in strontium titanate layers grown by high vacuum magnetron sputtering. Amount of hydrogen in the films and growth temperature; Microstructure of films deposited.

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics