Al[sub 2]O[sub 3+x]/Al interface formation by promoted oxidation using an alkali metal and

AUTHOR(S)
Huttel, Y.; Bourdie, E.; Soukiassian, P.; Mangat, P.S.; Hurych, Z.
PUB. DATE
May 1993
SOURCE
Applied Physics Letters;5/10/1993, Vol. 62 Issue 19, p2437
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Demonstrates the formation of alumina at room temperature by promoted aluminum oxidation using an alkali metal. Effect of sodium overlayer on aluminum thin film oxidation; Application of photoemission spectroscopy; Removal of the sodium catalyst by rapid thermal annealing.
ACCESSION #
4329723

 

Related Articles

  • Formation of ultradispersed systems based on sodium polyaluminates from thermal plasma flows. Tel'nova, G. B.; Grabis, Ya. P. // Glass & Ceramics;Nov2005, Vol. 62 Issue 11/12, p344 

    The process of synthesis of sodium β-alumina in a low-temperature nitric plasma is investigated. It is established that the main product of the plasmachemical reaction is sodium polyaluminate Na2O · nAl2O3 of an unknown structure, whose homogeneity range is within the interval of n =...

  • Effect of sodium hydroaluminosilicate (SHAS) structure on removal of impurities from alumina production solutions and on efficiency of regeneration processes. Suss, A. G.; Kuvyrkina, A. M.; Kuznetsova, N. V.; Panov, A. V. // Metallurgist;Nov2008, Vol. 52 Issue 11/12, p653 

    Both the additives contained in the solution and the temperature and duration of the process have an impact on the specific sodium hydroaluminosilicate (SAHS) form produced. The Cl– ion leads to the formation of sodalite structure, $\rm{SO}{_{4}^{2-}}$ leads to the formation of nosean...

  • Effect of crucible material on optical bandgap and activation energy of Na2O-CdO-P2O5 glasses. Altaf, M.; Chaudhry, M. A. // Journal of Materials Science;Aug2005, Vol. 40 Issue 15, p4019 

    In the sodium cadmium phosphate glasses, the effect of diffused alumina from alumina crucible has been assessed by measuring various properties such as mass density, refractive index, optical bandgap and dc conductivity. The results of measurements corresponding to glasses prepared in alumina...

  • New Possibilities for an Acid Method of Preparing Aluminum Oxide. Kashcheev, I.; Zemlyanoi, K.; Doronin, A.; Kozlovskikh, E. // Refractories & Industrial Ceramics;Jul2014, Vol. 55 Issue 2, p87 

    An effective method is proposed for processing complex alumina-containing materials of natural and technogenic origin with preparation of alkali-free highly active aluminum hydroxide as raw material for producing high-alumina materials, such as traditional engineering alumina, high-alumina...

  • Effect of Particle Size and Adsorbates on the L, L and L X-ray Absorption Near Edge Structure of Supported Pt Nanoparticles. Lei, Yu; Jelic, Jelena; Nitsche, Ludwig; Meyer, Randall; Miller, Jeffrey // Topics in Catalysis;Apr2011, Vol. 54 Issue 5-7, p334 

    Pt nano-particles from about 1 to 10 nm have been prepared on silica, alkali-silica, alumina, silica-alumina, carbon and SBA-15 supports. EXAFS spectra of the reduced catalysts in He show a contraction of the Pt-Pt bond distance as particle size is decreased below 3 nm. The bond length decreased...

  • Pore Structure, Permeability, and Alkali Attack Resistance of AlO-C Refractories. Xu, Yibiao; Sang, Shaobai; Li, Yawei; Ren, Bo; Zhao, Lei; Li, Yuanbing; Li, Shujing // Metallurgical & Materials Transactions. Part A;Jun2014, Vol. 45 Issue 6, p2885 

    AlO-C refractories were first fabricated in a coke bed at 1673 K (1400 °C) using tabular corundum, reactive alumina, carbon black, silicon, and microsilica as the starting materials and phenol resin as the binder. Then the alkali attack resistance of those materials was conducted in the...

  • Freeze cast carbon nanotube-alumina nanoparticle green composites. Lu, Kathy // Journal of Materials Science;Jan2008, Vol. 43 Issue 2, p652 

    CNT-Al2O3 nanoparticle suspensions without and with sodium dodecyl sulfate (SDS) were freeze-cast into green samples. SDS drastically improves Carbon nanotube (CNT) dispersion and CNT-Al2O3 nanocomposite homogeneity. Green density of the CNT-Al2O3 nanocomposites decreases with CNT addition....

  • Thermally induced structural modifications in sputtered C/Al2O3 multilayers. Veldkamp, M.; Zabel, H.; Morawe, Ch.; Arnscheidt, B. // Journal of Applied Physics;5/15/1998, Vol. 83 Issue 10, p5233 

    Provides information on an experiment investigating sputtered multilayers of carbon and alumina amorphous Al2O3. Methodology used to conduct the experiment; Recording of the Raman spectra at room temperature with an Ar-ion laser in a 180... scattering geometry; Detailed information on Raman...

  • Correction.  // Nature;9/24/2009, Vol. 461 Issue 7263, p451 

    A correction to the article "Aluminium arches" that was published in the 2009 issue is presented.

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics