Giant magnetoresistance in melt spun Cu-Co alloys

Wecker, J.; von Helmolt, R.; Schultz, L.; Samwer, K.
April 1993
Applied Physics Letters;4/19/1993, Vol. 62 Issue 16, p1985
Academic Journal
Examines the magnetoresistance (MR) in melt spun copper-cobalt alloys. Enumeration of parameters influencing MR; Effect of heat on the temperature dependence of MR; Percentage of MR in as-quenched ribbons.


Related Articles

  • Influence of Fe and Co additions on magnetization and magnetoresistivity of MnAu[sub 2] melt-spun alloys. Handstein, A.; Nenkov, K.; Ro¨ssler, U. K.; Mu¨ller, K.-H. // Journal of Applied Physics;5/1/2000, Vol. 87 Issue 9, p5789 

    Melt-spun MnAu[sub 2] ribbons modified by ternary magnetic additions (Fe and Co) show a large giant magnetoresistance (GMR) effect up to a magnetoresistance ratio MR={[R(H=7T)-R(0)/R(0)]} of the order of -10% at room temperature. Pure MnAu[sub 2] samples show a transition from positive...

  • Structural, Magnetic And Magneto-transport Studies In Melt-Spun Ni-Mn-Ga Ribbons. Rao, N. V. Rama; Ingale, Babita; Gopalan, R.; Chandrasekaran, V.; Chaubey, Niraj K.; Poddar, A.; Ranganathan, R.; Suresh, K. G. // AIP Conference Proceedings;4/24/2008, Vol. 1003 Issue 1, p201 

    Structural, magnetic and magneto-transport properties were investigated in the as-spun and annealed ribbons of Ni55Mn19.6Ga25.4. The structural transition from the ferromagnetic martensite phase to the paramagnetic austenite phase was observed at 309 K in the annealed ribbon. Large negative...

  • Magnetostriction of melt-spun Dy-Fe-B alloys. Lim, S. H.; Noh, T. H.; Kang, I. K.; Kim, S. R.; Lee, S. R. // Journal of Applied Physics;11/15/1994, Vol. 76 Issue 10, p7021 

    Focuses on a study which investigated the magnetostriction of melt-spun ribbons of Dy[subx](Fe[sub1-y]B[suby])[sub1-x] alloys as a function of the wheel speed during melt quenching. Experimental details; Results and discussion; Conclusion.

  • Magnetic studies in some melt spun amorphous Fe-Ho-B alloys. Krishnan, R.; El Marrakchi, O.; Lassri, H.; Rougier, P. // Journal of Applied Physics;6/1/1993, Vol. 73 Issue 11, p7599 

    Examines the magnetic properties of amorphous alloys prepared by melt spinning. Information on the magnetic studies in amorphous iron-erbium-boron alloys; Details on the experiment; Results of the study.

  • Preparation and magnetic properties of melt-spun Nd[sub 2]Fe[sub 14](BC)/α-Fe nanocomposite magnets. Wang, Z. C.; Davies, H. A.; Zhou, S. Z.; Zhang, M. C.; Qiao, Y. // Journal of Applied Physics;5/15/2002 Part 1, 2 & 3, Vol. 91 Issue 10, p7884 

    Phase evolution and magnetic properties of melt-spun Nd[sub 8]Fe[sub 86]B[sub 6-χ]C[sub χ] (χ = 0, 2, 4, 5, 6) alloy ribbons have been investigated. Increasing the C content was found to decrease the glass-forming tendency of as-spun ribbons. For samples with low C content (χ...

  • High-coercivity (NdDy)2(FeNb)14B-alpha-Fe nanocrystalline alloys. Wang, Zuocheng; Zhang, Maocai // Journal of Applied Physics;4/17/1997, Vol. 81 Issue 8, p5097 

    Reports that high coercivity, high remanence, and high energy products have been obtained in melt-spun (NdDy)2(FeNb)14B-alpha-Fe nanocrystalline alloys with a mixture of hard and soft magnetic phases. Categories of the samples studied; Mult-spun ribbons' amorphous structure.

  • High coercivity in non-rare-earth containing alloys. Gao, C.; Wan, H.; Hadjipanayis, G. C. // Journal of Applied Physics;5/1/1990, Vol. 67 Issue 9, p4960 

    Presents information on a study which analyzed large coercive fields obtained in melt-spun cobalt zirconium (hafnium)-boron based alloys. Preparation of bulk samples from raw materials of at least 99.9% by using arc melting; Utilization of a Dupoint 1090 differential scanning calorimeter;...

  • High coercivity of melt–spun Sm2Fe15Al2C1.5 compound. Zhang, Jun-Xian; Cheng, Zhao-Hua; Shen, Bao-Gen // Journal of Applied Physics;4/15/1996, Vol. 79 Issue 8, p5528 

    Investigates the hard magnetic properties of melt-spun Sm[sub2]Fe[sub15]Al[sub2]C[sub1.5] alloys. Effect of the substitution of gallium or aluminum; X-ray diffraction patterns; Anisotropy field and coercivity of compounds.

  • Electrical and Magnetic Transport Properties of Nanocrystalline FeSiBCuNb Alloy. Muhammad, Deen; Khan, F.; Farabi, H.; Jubaer Alam, M. // Journal of Superconductivity & Novel Magnetism;Jun2014, Vol. 27 Issue 6, p1525 

    Electrical and magnetic transport properties of FeSiBCuNb (FINEMET) metallic ribbons prepared by standard melt-spinning technique have been investigated through dc and ac magnetic as well as electrical properties. FeSiBCuNb shows conventional anisotropic magnetoresistance (MR) which is found to...


Read the Article


Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics