TITLE

Synthesis and processing of silicon nanocrystallites using a pulsed laser ablation supersonic

AUTHOR(S)
Werwa, E.; Seraphin, A.A.
PUB. DATE
April 1994
SOURCE
Applied Physics Letters;4/4/1994, Vol. 64 Issue 14, p1821
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Investigates nanostructured silicon materials by pulsed laser ablation supersonic expansion technique. Use of transmission electron microscopy for particle size measurements; Confirmation of the silicon diamond cubic crystal structure by x-ray diffraction; Exhibition of visible photoluminescence in nanocrystallites.
ACCESSION #
4255091

 

Related Articles

  • Photoluminescent and Electronic Properties of Nanocrystalline Silicon Doped with Gold. Kaganovich, �. B.; Kizyak, I. M.; Kirillova, S. I.; Manoilov, �. G.; Primachenko, V. E.; Svechnikov, S. V.; Venger, E. F. // Semiconductors;Sep2002, Vol. 36 Issue 9, p1027 

    Doping nanocrystalline silicon (nc-Si) films grown by laser ablation with gold leads to a considerable suppression of the nonradiative recombination of the charge carriers and excitons, an increase in the intensity and stability of the visible photoluminescence, and enhancement of the low-energy...

  • Time response of 1.54 mum emission from highly Er-doped nanocrystalline Si thin films prepared... Komuro, Shuji; Katsumata, Tooru; Morikawa, Takitaro; Xinwei Zhao; Isshiki, Hideo; Aoyagi, Yoshinobu // Applied Physics Letters;1/18/1999, Vol. 74 Issue 3, p377 

    Investigates the time response of 1.54 micrometer emission from highly Er-doped nanocrystalline silicon thin films prepared by laser ablation. Photoluminescence originating from intra-4f shell transitions in Er[sup 3+] ions; Indications of the time response measurements; Excitation of...

  • Formation of core-shell structured silicon nanoparticles during pulsed laser ablation. Ikurou Umezu; Yusuke Nakayama; Akira Sugimura // Journal of Applied Physics;May2010, Vol. 107 Issue 9, p094318-1 

    We performed pulsed laser ablation of Si target in nitrogen background gas and found that core-shell structured nanoparticles can be prepared without postsurface treatment. The predominant ejected species from the target at free expansion region is Si, and N related species appears at the point...

  • Morphology of Si nanowires fabricated by laser ablation using gold catalysts. Wang, K.; Chung, S. Y.; Kim, D. // Applied Physics A: Materials Science & Processing;2004, Vol. 79 Issue 4-6, p895 

    Si nanowires (NWs) were fabricated successfully by laser ablation using Au as catalyst. Si wafers were used as the collector. The diameters of Si NWs ranged from 20 to 150 nm. Different forms of Si NWs were observed at different local sites inside a furnace: Si NWs with a high aspect ratio of...

  • Phosphorus doping and hydrogen passivation of donors and defects in silicon nanowires synthesized by laser ablation. Fukata, N.; Chen, J.; Sekiguchi, T.; Matsushita, S.; Oshima, T.; Uchida, N.; Murakami, K.; Tsurui, T.; Ito, S. // Applied Physics Letters;4/9/2007, Vol. 90 Issue 15, p153117 

    Phosphorus (P) doping was performed during the synthesis of silicon nanowires (SiNWs) by laser ablation. At least three types of signals were observed by electron spin resonance (ESR) at 4.2 K. Phosphorus doping into substitutional sites of crystalline Si in SiNWs was demonstrated by the...

  • Fabrication of uniform nanogrooves on 6H-SiC by femtosecond laser ablation. Kim, Sung; Sohn, Ik-Bu; Jeong, Sungho // Applied Physics A: Materials Science & Processing;Jan2011, Vol. 102 Issue 1, p55 

    The fabrication of parallel deep nanogrooves on 6H-SiC by femtosecond laser ablation ( λ=785 nm) is reported. The periodicity of the nanogrooves was measured to be about 200±20 nm and the depth exceeded 15 μm. The nanogrooves have high uniformity in size and pattern over the entire...

  • Solubility enhancement and epitaxial core-shell structure of Si-doped ZnO via a specific pulsed laser ablation route. Huang, Chang-Ning; Chen, Shuei-Yuan; Zheng, Yuyuan; Shen, Pouyan // Applied Physics A: Materials Science & Processing;Sep2015, Vol. 120 Issue 3, p1033 

    Wurtzite (W)-type ZnO nanocondensates and particulates with enhanced solid solubility of Si and special defect nanostructures were synthesized via pulsed laser ablation of ZnSiO/ZnO composite target under a relatively high peak power density of 1.4 × 10 W/cm in high vacuum (3.5 × 10...

  • Low-fluence femtosecond-laser interaction with a Mo/Si multilayer stack. Höche, T.; Ruthe, D.; Petsch, T. // Applied Physics A: Materials Science & Processing;2004, Vol. 79 Issue 4-6, p961 

    Nanostructural damage caused by low-fluence, non-ablating femtosecond laser irradiation of Mo/Si multilayer stacks is studied by cross-sectional transmission electron microscopy. A laterally homogeneous modification of the multilayer structure is observed including a complete intermixing of...

  • Correlation between photoluminescence properties and morphology of laser-ablated Si/SiO[sub x] nanostructured films. Kabashin, A. V.; Sylvestre, J.-P.; Patskovsky, S.; Meunier, M. // Journal of Applied Physics;3/1/2002, Vol. 91 Issue 5, p3248 

    Pulsed laser ablation in an inert gas has been used to fabricate films containing silicon nanocrystals. We show that film microstructure is one of the main factors, determining long-term photoluminescence (PL) properties. Films with different porosity were found to exhibit PL signals with quite...

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics