Scaling of critical currents in high-temperature superconducting superlattices and thin films

Fernandes, A.A.R.; Chan, I.N.
December 1992
Applied Physics Letters;12/28/1992, Vol. 61 Issue 26, p3181
Academic Journal
Measures the transport critical current densities in superconducting superlattices and thin films. Dependence of temperature on critical current density; Universality of pinning mechanisms in the systems; Applicability of the scaling law for RBa[sub 2]Cu[sub 3]O[sub x] materials.


Related Articles

  • Transport critical current density and electrical characterization of patterned high-Tc superconducting thin films prepared by metallo-organic decomposition. Lubberts, G. // Journal of Applied Physics;7/15/1990, Vol. 68 Issue 2, p688 

    Focuses on a study which measured resistivity and transport critical current density as a function of temperature for patterned YBa[sub2]Cu[sub3]O[sub7] and Bi[sub2]Sr[sub2]CaCu[sub2]O[sub8+∞] superconducting thin films on single crystal MgO substrates. Formation of superconducting ceramic...

  • Mixed-state behavior in large magnetic fields of high-temperature superconducting films prepared... McIntyre, Paul C.; Cima, Michael J.; Liebenberg, Donald H.; Francavilla, Thomas L. // Applied Physics Letters;5/6/1991, Vol. 58 Issue 18, p2033 

    Demonstrates that superconducting films of Ba[sub 2]YCu[sub 3]O[sub 7-x] prepared by metalorganic deposition have large critical current densities in high magnetic fields. Current-voltage characteristics; Zero field critical current density.

  • High critical currents in epitaxial YBa2Cu3O7-x thin films on silicon with buffer layers. Wu, X. D.; Inam, A.; Hegde, M. S.; Wilkens, B.; Chang, C. C.; Hwang, D. M.; Nazar, L.; Venkatesan, T.; Miura, S.; Matsubara, S.; Miyasaka, Y.; Shohata, N. // Applied Physics Letters;2/20/1989, Vol. 54 Issue 8, p754 

    As-deposited superconducting thin films (∼0.1 μm) of YBa2Cu3O7-x have been prepared by pulsed laser deposition on (100) Si with buffer layers of BaTiO3/MgAl2O4. X-ray diffraction studies reveal that the films grow epitaxially with the c axis preferentially oriented normal to the...

  • Shear-limited flux pinning studied in superconducting thin-film devices. Pruymboom, A.; Kes, P. H.; van der Drift, E.; Radelaar, S. // Applied Physics Letters;2/22/1988, Vol. 52 Issue 8, p662 

    We report critical-current measurements on superconducting devices containing nanometer-scale artificially structured channels of low pinning which simulate microstructures in technical superconductors. Our observations uniquely demonstrate the role of the grain morphology for flux pinning in...

  • Focused ion beam high T[sub c] superconductor dc SQUIDS. Zani, M.J.; Luine, J.A.; Simon, R.W.; Davidheiser, R.A. // Applied Physics Letters;7/8/1991, Vol. 59 Issue 2, p234 

    Investigates the critical current density reduction of high-temperature superconductor thin films. Irradiation of thin films using high-energy focused ion beam; Use of direct current superconducting quantum interference device (SQUID) structure; Percentage of SQUID critical current modulation.

  • Metalorganic deposition of high critical current thin films in the Bi-Sr-Ca-Cu-O system on.... Golden, S.J.; Lange, F.F. // Applied Physics Letters;7/20/1992, Vol. 61 Issue 3, p351 

    Fabricates a superconducting thin films of the two copper-layer phase in the lead-doped Bi-Sr-Ca-Cu-O system. Effect of heat treatment on the thin films; Measurements of the critical current densities; Epitaxial growth of the film; Production of the ethyl hexanoate precursor solutions;...

  • Epitaxial growth and critical current density of thin films of YBa2Cu3O7-x on LaAlO3 substrates. Mogro-Campero, A.; Turner, L. G.; Hall, E. L.; Garbauskas, M. F.; Lewis, N. // Applied Physics Letters;6/26/1989, Vol. 54 Issue 26, p2719 

    Thin films of the high-temperature superconductor YBa2 Cu3 O7-x have been produced on (100) LaAlO3 substrates by coevaporation and furnace annealing. A 14-μm-wide and 400-μm-long constriction patterned on a 0.8-μm-thick film had a zero resistance transition temperature of 90 K, a...

  • Critical current and flux pinning near Tc of a YBa2Cu3O7 thin film. Qiu, X. G.; Cui, C. G.; Li, S. L.; Liu, M. X.; Li, J.; Zhang, Y. Z.; Zhao, Y. Y.; Xu, P.; Li, L.; Chen, L. F.; Chen, P. F.; Li, N.; Liu, G. T. // Journal of Applied Physics;8/15/1991, Vol. 70 Issue 4, p2461 

    Focuses on a study which measured the voltage versus current of a high-quality YBa[sub2]Cu[sub3]O[sub7-x] thin film at temperatures under different magnetic fields. Properties of the materials; Description of the experimental set-up; Findings and conclusions.

  • Spatial variation of the critical current density of the high Tc superconducting thin films. Feng, Y. J.; Cheng, Q. H.; Wu, P. H.; Liu, H. M. // Journal of Applied Physics;12/1/1992, Vol. 72 Issue 11, p5350 

    Examines the spatial distribution of the superconducting properties of high Curie temperature thin films. Value of the maximum local critical current density; Electron-beam irradiation of the thin film sample; Use of the four-probe transport measurement of the critical current density.


Read the Article


Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics