Electrochromic properties of vanadium pentoxide thin films prepared by new wet process

Nagase, Katsumi; Shimizu, Youichi
February 1992
Applied Physics Letters;2/17/1992, Vol. 60 Issue 7, p802
Academic Journal
Demonstrates the electrochromic properties of vanadium pentoxide thin films prepared by an organic vanadium solution by a spin-coating method. Demonstration of electrochromism in the heat-treated films; Comparison of the memory characteristics among the yellow, green and blue colors; Effectiveness of the process in preparing the films.


Related Articles

  • Structural, optical and electrochromic properties of sol-gel V 2 O 5 thin films. Benmoussa, M.; Outzourhit, A.; Jourdani, R.; Bennouna, A.; Ameziane, E.L. // Active & Passive Electronic Components;Dec2003, Vol. 26 Issue 4, p245 

    Vanadium pentoxide thin films are prepared by the sol-gel route by dissolving V 2 O 5 powder (99.5% purity) in H 2 O 2 solution. The solution is spin-coated on glass substrates for optical (UV-VIS-NIR) and XRD analysis, and on ITO-coated glass substrates for electrochromic measurements. The...

  • Structure and optical absorption of LiyV2O5 thin films. Talledo, A.; Andersson, A. M.; Granqvist, C. G. // Journal of Applied Physics;3/1/1991, Vol. 69 Issue 5, p3261 

    Discusses the structure and associated optical absorption features in lithiated vanadium pentoxide thin films made by sputtering and electrochemical post treatment. Outline of the preparation of V[sub2]O[sub5] thin films by reactive direct current magnetron sputtering onto...

  • Lithium vanadium bronze thin films for electrochromic applications. Green, Mino; Pita, K. // Journal of Applied Physics;4/15/1997, Vol. 81 Issue 8, p3592 

    Reports that chemically stable, well adhering films of fine grained polycrystalline stoichiometric V2O5 can be prepared by vacuum deposition. Thin film preparation; Vanadium pentoxide; Lithium vanadium bronze; Determination of lithium stoichiometry; Electrochemical insertion and extraction;...

  • Electrical and optical properties of thin films of hydrated vanadium pentoxide featuring electrochromic effect. Yakovleva, D. S.; Malinenko, V. P.; Pergament, A. L.; Stefanovich, G. B. // Technical Physics Letters;Dec2007, Vol. 33 Issue 12, p1022 

    Thin films of hydrated vanadium pentoxide (V2O5 · nH2O) exhibit the phenomenon of electrochromism, whereby a film reversibly changes its color under the action of an applied electric field. A specific feature of this phenomenon is that it takes place in a “dry” planar system, in...

  • Stable and erasable patterning of vanadium pentoxide thin films by atomic force microscope nanolithography. Iwanaga, Shiho; Darling, R. B.; Cobden, D. H. // Applied Physics Letters;3/28/2005, Vol. 86 Issue 13, p133113 

    Long lasting colored pattern formation on sol–gel deposited vanadium pentoxide (V2O5) thin films is demonstrated by atomic force microscope (AFM) nanolithography. The films can be locally colorized by application of a positive dc bias voltage on the conductive AFM tip. The patterns can be...

  • Microstructure study of amorphous vanadium oxide thin films using raman spectroscopy. Lee, Se-Hee; Cheong, Hyeonsik M.; Je Seong, Maeng; Liu, Ping; Tracy, C. Edwin; Mascarenhas, Angelo; Pitts, J. Roland; Deb, Satyen K. // Journal of Applied Physics;8/15/2002, Vol. 92 Issue 4, p1893 

    Microstructural changes of amorphous V[sub 2]O[sub 5] films with lithium intercalation are studied using Raman-scattering measurements. The Raman spectra of as-deposited films show two broad peaks around at 520 and 650 cm[sup -1], due to the stretching modes of the [sub V]3-O and V[sub 2]-O...

  • Influence of film thickness on texture and electrical and optical properties of room temperature deposited nanocrystalline V2O5 thin films. Singh, Preetam; Kaur, Davinder // Journal of Applied Physics;Feb2008, Vol. 103 Issue 4, p043507 

    Nanocrystalline V2O5 thin films have been grown at low temperature on glass substrates by dc magnetron sputtering using a vanadium metal target. Film thickness was found to have a great impact on the orientation, shape, and size of the crystallites of these films. X-ray diffraction (XRD)...

  • Gas-sensing Properties of Pt-V2O5 Thin films for Ethanol Detection. Kruefu, Viruntachar; Pookmanee, Pusit; Wisitsoraat, Anurat; Phanichphant, Sukon // Key Engineering Materials;2015, Vol. 659, p259 

    In the present work, vanadium pentoxide (V2O5) nanoparticles have been investigated for monitoring ethanol (C2H5OH) at ppm levels in air. A one-step flame spray pyrolysis (FSP) process has been applied for the synthesis of vanadium pentoxide (V2O5) and platinum-loaded vanadium pentoxide...

  • Sun roof. Baker, Berenice // Engineer (00137758);1/29/2007, Vol. 293 Issue 7716, p8 

    The article reports the findings of the government-funded study in Great Britain which points that roofs painted with dye-sensitized photovoltaic coatings can be made into solar power generators. According to David Worsely, one of the researchers, dye-sensitized semi-conductor cells give...


Read the Article


Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics