TITLE

Microwave surface resistance of spin-cast YBa[sub 2]Cu[sub 3]O[sub 7-x] thin films on

AUTHOR(S)
Peir-Yung Chu; Buchanan, Relva C.
PUB. DATE
December 1993
SOURCE
Applied Physics Letters;12/20/1993, Vol. 63 Issue 25, p3512
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Examines the microwave properties of spin-cast YBa[sub 2]Cu[sub 3]O[sub 7-x] thin films on LaAlO[sub 3] substrates. Methods used to characterize high temperature superconducting thin films; Preparation of the thin films by carboxylate solution precursors; Results of the reactive liquid phase sintering mechanism.
ACCESSION #
4240906

 

Related Articles

  • Effect of sintering temperature under high pressure on the superconductivity of MgB[sub 2]. Jung, C. U.; Park, Min-Seok; Kang, W. N.; Kim, Mun-Seog; Kim, Kijoon H. P.; Lee, S. Y.; Lee, Sung-Ik // Applied Physics Letters;6/25/2001, Vol. 78 Issue 26, p4157 

    We report on the effect of sintering temperature on the superconductivity of MgB[sub 2] pellets prepared under a high pressure of 3 GPa. The superconducting properties of the nonheated MgB[sub 2] were poor. However, as the sintering temperature increased, the superconducting properties were...

  • Superconducting Properties and Microstructure of Nanocrystalline MgB Bulk Prepared by Sintering of Ball-Milled Powders. Sun, Yaxin; Zhu, Longhui; Song, Xiumei; Yu, Dongli; Liu, Yanguo // Journal of Superconductivity & Novel Magnetism;Aug2012, Vol. 25 Issue 6, p1735 

    Ultrafine nanostructured MgB bulks with an average grain size less than 10 nm have been fabricated by high-energy ball milling and subsequent high pressure sintering. Microstructural evolution in MgB subjected to high-energy ball milling has been investigated by means of X-ray diffraction (XRD)....

  • High pressure-high temperature treatment of MT-MeBCO (Me=Y,Nd,Sm), high-pressure sintering of Y123 and synthesis of MgB[sub 2]. Prikhna, T. A.; Gawalek, W.; Habisreuther, T.; Moshchil, V. E.; Surzhenko, A. B.; Melnikov, V. S.; Dub, S. N.; Nagorny, P. A.; Sergienko, N. V.; Krabbes, G.; Savchuk, Ya. M.; Schmidt, Ch.; Dellith, J.; Vlasenko, A. V. // AIP Conference Proceedings;2002, Vol. 614 Issue 1, p398 

    A short-term treatment, sintering or synthesis of high-temperature superconductors (HTS) under high pressures allow us to retain oxygen in the structure of Y123-type superconductors or to suppress the evaporation of Mg during synthesis of MgB[sub 2] and to attain practically theoretical density...

  • Small field behavior of critical current in Y1Ba2Cu3O7 sintered samples. Paternò, G.; Alvani, C.; Casadio, S.; Gambardella, U.; Maritato, L. // Applied Physics Letters;8/15/1988, Vol. 53 Issue 7, p609 

    Critical currents carried by sintered Y1Ba2Cu3O7 superconducting samples have been measured at different temperatures close to the critical temperature Tc. The effects of an applied magnetic field perpendicular to the current direction have been investigated. A strong reduction of the dc current...

  • (Tl, Pb, Bi)Sr2Ca2Cu3Oz superconductors with zero resistance at 120 K. Kaneko, Tetsuyuki; Wada, Takahiro; Yamauchi, H.; Tanaka, Shoji // Applied Physics Letters;3/26/1990, Vol. 56 Issue 13, p1281 

    We have synthesized new superconductors of nearly single phase with zero-resistance temperatures around 120 K employing a novel method for sintering. The samples included a nominal composition of (Tl0.64Pb0.2Bi0.16)Sr2Ca3Cu4Oz. This sample was prepared from the mixture of presynthesized...

  • Third harmonics in the minor loop of a sintered Y-Ba-Cu-O superconducting disk and its dc-field dependence. Okamoto, K.; Makino, Y.; Watanabe, N.; Rao, K. V. // Journal of Applied Physics;5/1/1990, Vol. 67 Issue 9, p4539 

    Presents a study that investigated the low-field M-H minor loop of a sintered yttrium barium[sub2] copper[sub3] oxygen[sub7-δ] superconducting disk at liquid nitrogen temperatures both in the zero-field and field-cooled states. Experimental details; Experimental results and discussion;...

  • Shielding of pulsed magnetic fields with already sintered 1 μm sized powder-pressed Bi-based superconducting rings. Matsuzawa, Hidenori; Mikami, Koji; Ibi, Akira // Applied Physics Letters;6/11/2001, Vol. 78 Issue 24, p3854 

    To confirm a ferrite-core model for the superconducting rings (supertrons) to focus and guide electron current beams, we examined a bismuth-based ring into the configuration of which already sintered 1 μm sized 2223-phase powders were cold-isostatic pressed. No additional sintering was...

  • Superconductivity Enhancement in FeO Doped YBaCuO. Dong, Xueguang; An, Pengfei; Zhang, Jing; Zhang, Hongguang; Li, Yongtao; Liu, Hao; Ge, Xiaopeng; Li, Qi // Journal of Superconductivity & Novel Magnetism;Mar2014, Vol. 27 Issue 3, p693 

    Flux pinning can lead to the enhancement of J in superconductor. In order to study the effect of magnetic particles on superconductivity, the composites of (YBaCuO)(FeO) and (YBaCuO)( α-FeO) are synthesized with former sintered at different temperatures. The field-cooling measurements show...

  • Superconductivities of n-type Nd[sub 1.85]Ce[sub 0.15]CuO[sub 4-y] prepared under high pressure. Jin, C.Q.; Yao, Y.S.; Wu, B.Q.; Xu, Y.F.; Liu, S.C.; Wang, W.K. // Applied Physics Letters;12/23/1991, Vol. 59 Issue 26, p3479 

    Examines the preparation of a bulk n-type NdCeCuCo superconductor using a high-pressure high temperature sintering procedure. Reduction of the weak link effects; Measurement of the resistance of the superconductors; Demonstration of a higher onset and zero resistance temperatures.

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics