Phase transformation of cobalt induced by ball milling

Huang, J.Y.; Wu, Y.K.
January 1995
Applied Physics Letters;1/16/1995, Vol. 66 Issue 3, p308
Academic Journal
Reports the phase transformation of pure element cobalt induced by ball milling (BM). Suggestion of a possible mechanism for phase transformation; Significance of the BM technique; Diffraction x-ray pattern of elemental cobalt; Determination of cobalt phase formation by structure defects accumulation.


Related Articles

  • Response to 'Comment on 'Phase transformation of cobalt induced by ball milling'. Huang, J.Y.; Wu, Y.K. // Applied Physics Letters;9/25/1995, Vol. 67 Issue 13, p1945 

    Responds to comments made on an article on the phase transformation of cobalt induced by ball milling. Formation of a heavily induced hcp phase; Transformation of random close packed phase to hcp phase at the lowest intensity; Dependence of Fe contamination on mill intensity.

  • Nonequilibrium phase transformation and magnetic properties of Ni3Sn2 during mechanical milling. Zhou, G. F.; Di, L. M.; Bakker, H. // Journal of Applied Physics;2/1/1993, Vol. 73 Issue 3, p1521 

    Focuses on a study which monitored nonequilibrium phase transformation in stoichiometric Ni[sub3]Sn[sub2] during mechanical impact in a high-energy ball mill. Experimental procedure; Structural relationships; Experimental results; Discussion.

  • High-temperature phase transformations of iron anhydrous ammonia system realized by ball milling at room temperature. Chen, Y.; Williams, J. S.; Wang, G. M. // Journal of Applied Physics;4/15/1996, Vol. 79 Issue 8, p3956 

    Presents a study that investigated high-temperature phase transformations of iron anhydrous ammonia system realized by ball milling at room temperature. Performance of ball milling process and other milling experiments; Analysis of x-ray diffraction patterns taken from the milled samples; Phase...

  • A model-based approach for monitoring of shape deviations in peripheral milling. Krüger, M.; Denkena, B. // International Journal of Advanced Manufacturing Technology;Aug2013, Vol. 67 Issue 9-12, p2537 

    This paper presents a model-based approach for monitoring of shape deviations for milling operations. In order to detect occurring shape deviations of the machined workpiece during the milling process, different kinds of process models are presented and discussed for their application on...

  • Fabrication of 13Cr-2Mo Ferritic/Martensitic Oxide-Dispersion-Strengthened Steel Components by Mechanical Alloying and Spark-Plasma Sintering. Bogachev, I.; Grigoryev, E.; Khasanov, O.; Olevsky, E. // JOM: The Journal of The Minerals, Metals & Materials Society (TM;Jun2014, Vol. 66 Issue 6, p1020 

    The outcomes of the mechanical alloying of 13Cr-2Mo ferritic/martensitic steel and yttria (oxide-dispersion-strengthened steel) powders in a ball mill are reported in terms of the powder particle size and morphology evolution. The optimal ball mill rotation speed and the milling time are...

  • Polyamorphous transition in amorphous fullerites C. Borisova, P.; Agafonov, S.; Glazkov, V.; D'yakonova, N.; Somenkov, V. // Crystallography Reports;Dec2011, Vol. 56 Issue 7, p1123 

    Samples of amorphous fullerites C have been obtained by mechanical activation (grinding in a ball mill). The structure of the samples has been investigated by neutron and X-ray diffraction. The high-temperature (up to 1200°C) annealing of amorphous fullerites revealed a polyamorphous...

  • One-step fastest method of nanocrystalline CuAlS chalcopyrite synthesis, and its nanostructure characterization. Ghosh, B.; Pradhan, S. // Journal of Nanoparticle Research;Jun2011, Vol. 13 Issue 6, p2343 

    Nanocrystalline CuAlS chalcopyrite has been mechanosynthesized at room temperature for the first time by ball milling the stoichiometric mixture of elemental of Cu, Al, and S powders under argon atmosphere. Initially, the CuAlS phase is formed by solid state reaction of elemental powders within...

  • Neutron diffraction study of the interaction of iron with amorphous fullerite. Borisova, P.; Agafonov, S.; Blanter, M.; Somenkov, V. // Physics of the Solid State;Jan2014, Vol. 56 Issue 1, p199 

    The amorphous fullerite C has been prepared by mechanical activation (grinding in a ball mill), and its interaction with iron during sintering of powders with 0-95 at % Fe has been studied. After sintering in the range 800-1200°C under a pressure of 70 MPa, the samples have nonequilibrium...

  • Influence of Ball-Milling Treatment of B Original Powder on the Phase Formation and Critical Current Density of Graphite Doped MgB $$_{2}$$. Su, Xiaocheng; Jiang, Qingguo; Zuo, Anying // Journal of Low Temperature Physics;Oct2014, Vol. 177 Issue 1/2, p8 

    In present work, the sintering process and superconducting properties of graphite doped MgB $$_{2}$$ prepared with milled B original powder were investigated. It is found that ball milling treatment of B original powder obviously suppresses the solid-solid reaction between Mg and B, whereas it...


Read the Article


Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics