TITLE

In vitro Corrosion behavior of 13 prosthodontic alloys

AUTHOR(S)
Canay, Şenay; Öktemer, Müjgan
PUB. DATE
April 1992
SOURCE
Quintessence International;Apr1992, Vol. 23 Issue 4, p279
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
The corrosion behavior of 12 high-gold, low-gold, palladium-silver, and nickel-chromium alloys was tested using electrochemical techniques. A 22-carat-gold alloy was used as a control. High-gold alloys were extremely resistant to corrosion, but the resistance of the alloys decreased with decreasing nobility (from high-gold, to palladium-silver, to low-gold, to nickel-chromium alloys). Tests were also made to determine the type of corrosive attack; nickel-chromium alloys exhibited pitting, and palladium-silver alloys demonstrated the selective dissolution of the silver-rich phases. The corrosion resistance of noble alloys was far superior to that of nickel-chromium-based alloys; therefore, the palladium-silver alloys, which have a moderate price range, may be more suitable for restorations.
ACCESSION #
38699021

 

Related Articles

  • Polarization-Corrosion Behavior of Commercial Gold- and Silver-base Casting Alloys in Fusayama Solution. JOHNSON, D. L.; RINNE, V. W.; BLEICH, L. L. // Journal of Dental Research;Dec1983, Vol. 62 Issue 12, p1221 

    Based on polarization measurements, high Au alloys are highly corrosion-resistant and exhibit the lowest corrosion rates; intermediate Au, Ag, and Pd alloys with Cu are passive but exhibit higher corrosion rates. Twenty weight percent (w/o) In-Ag alloys exhibit active corrosion behavior at...

  • Casting Accuracy of Nickel-Chromium Alloys: Marginal Discrepancies. DUNCAN, J. DAVID // Journal of Dental Research;Jul1980, Vol. 59 Issue 7, p1164 

    This article discusses the results of a research study conducted to determine the casting accuracy, finishing characteristics, porcelain-to-alloy bonding, and corrosion sensitivities of four nickel-chromium alloys for use in casting crown and bridge prostheses. The study finds nickel-chromium...

  • ELECTROCHEMICAL INVESTIGATIONS ON THE BEHAVIOUR OF Ni-Cr BASED DENTAL MATERIALS IN THE SODIUM CHLORIDE -- OXALIC ACID -- LACTIC ACID SYSTEM. Sutiman, Daniel; Cailean, Adrian; Mareci, Daniel; Nechita, Mircea Teodor // Environmental Engineering & Management Journal (EEMJ);2007, Vol. 6 Issue 3, p231 

    The corrosion behaviour of three commercial nickel-chromium based dental materials was investigated by electrochemical methods in a corroding mixture of sodium chloride, oxalic acid and lactic acid. In order to establish electrochemical parameters of the corrosion process, linear and cyclic...

  • Corrosion resistance and wear resistance of Ni-Cr alloy after coating titanium nitride (TiN) in oral containing fluorine environment. WENG Wei-min; YU Wei-qiang; SHAN Wei-lan; ZHANG Fu-qiang // Shanghai Journal of Stomatology;Dec2010, Vol. 19 Issue 6, p621 

    No abstract available.

  • New Approach for Evaluating Metal-Porcelain Interfacial Bonding. Suansuwan, Napa; Swain, Michael Vincent // International Journal of Prosthodontics;Nov/Dec1999, Vol. 12 Issue 6, p547 

    Purpose: The purpose of this study was to evaluate the bonding characteristics of porcelain-fused-to-metal (PFM) systems by determining the strain energy release rate associated with interface fracture of porcelain and metals. Materials and Methods: Porcelain-veneered metal plates cast from...

  • Evaluation of 2 thione primers and 3 resin adhesives for silver-palladium-copper-gold alloy bonding. Koishi, Yoshikazu; Tanoue, Naomi; Yanagida, Hiroaki; Atsuta, Mitsuru; Nakamura, Mitsuo; Matsumura, Hideo // Quintessence International;May2006, Vol. 37 Issue 5, p395 

    Objective: The purpose of this study was to evaluate 2 thione primers and 3 resin adhesives for enhancement of bonding strength to a silver-palladium-copper-gold alloy. Method and Materials: Two different sized disk specimens (10- and 8-mm diameter by 2.5-mm thick) were prepared from a...

  • Structure, Corrosion, and Tarnishing of Ag-Pd-Cu Alloys. NIEMI, L.; HERØ, H. // Journal of Dental Research;Sep1985, Vol. 64 Issue 9, p1163 

    The structure of Ag-Pd-Cu-Au-Zn alloys can be expected to have an influence on their corrosion and tarnish resistance. Four experimental Ag-based alloys (I-IV) with varying Pd/Ag ratios were studied by scanning electron microscopy (SEM), microprobe analyses, and x-ray diffraction analyses. Both...

  • SOLDER JOINTS ON PLATED RUSTLESS ALLOYS. BIEN, SAUL M.; AYERS, JR., HERBERT D. // Journal of Dental Research;Apr1958, Vol. 37 Issue 2, p368 

    The article presents research into the nature of the bonds created by solder joints on plated rustless dental alloys. Researchers examine joints where solder was melted over a thin electrochemical deposition of gold on rustless alloy. The procedure produced 3 classifications of bonds...

  • Corrosion of Gold and Amalgam Placed in Contact with Each Other. FUSAYAMA, TAKAO; KATAYORI, TSUNEO; NOMOTO, SUNAO // Journal of Dental Research;Sep1963, Vol. 42 Issue 5, p1183 

    This article reports on the corrosion of dental amalgams and gold amalgams. The article discusses the use of these amalgams in dental restorations and how galvanic currents can be produced when the dissimilar metals come into contact in saliva. Information is presented on galvanic pain in the...

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics