Flux-flow critical-state susceptibility of superconductors

AUTHOR(S)
Chen, D.-X.; Pardo, E.; Sanchez, A.
PUB. DATE
June 2005
SOURCE
Applied Physics Letters;6/13/2005, Vol. 86 Issue 24, p242503
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
The field-amplitude Hm and circular frequency ω dependent ac susceptibility, χ=χ′-jχ″, of a hard superconducting cylinder with flux-flow type current-voltage characteristic is calculated. A remarkable feature of the resultant χ(Hm,ω) is that both the maximum χ″, χm″, and d lg Hm(χm″)/d lg ω increase with increasing ω. This behavior is observed in actual Bi-2223/Ag tapes and YBa2Cu3O7-δ-coated conductors. Our result provides a useful tool to study the intergranular critical state in high-temperature superconductors.
ACCESSION #
17452694

 

Related Articles

  • Irreversibility line and thermally activated flux flow in La1.6-xNd0.4SrxCuO4 films. Liu, Y.; Li, X. G. // Journal of Applied Physics;3/1/2006, Vol. 99 Issue 5, p053903 

    The resistive transition broadening of the c-axis oriented La1.6-xNd0.4SrxCuO4 epitaxial films (x=0.1, 0.12, 0.14, and 0.16) has been systematically investigated under magnetic fields up to 14 T for both H⊥c and H∥c configurations. For H∥c, the irreversibility line corresponds to...

  • Effect of diffusion-annealing time on magnetoresistivity of Cu-diffused bulk MgB superconductors with experimental and theoretical approaches. Dogruer, M.; Yildirim, G.; Terzioglu, C. // Journal of Materials Science: Materials in Electronics;Mar2013, Vol. 24 Issue 3, p958 

    This study reports the role of various annealing time such as 0.5, 1, 1.5 and 2 h on the flux pinning mechanism, physical and superconducting properties of Cu-diffused bulk MgB superconductors prepared at 850 °C with the aid of the magnetoresistivity measurements performed in the magnetic...

  • Threshold stresses for motion of dislocations in extrinsic semiconductors. Petukhov, B. // Semiconductors;Jun2007, Vol. 41 Issue 6, p625 

    It is shown that statistical fluctuations in the distribution of impurity atoms adsorbed at dislocations lead to the existence of a dislocation-mobility threshold with a magnitude σth dependent on temperature and interaction between impurities. In the low-temperature region, σth can...

  • Large exchange bias and high stability of CoFe/CrPt films with L10 CrPt as the pinning layer. Dai, B.; Cai, J. W.; Lai, W. Y.; An, Y. K.; Mai, Z. H.; Shen, F.; Liu, Y. Z.; Zhang, Z. // Applied Physics Letters;8/29/2005, Vol. 87 Issue 9, p092506 

    We have studied an antiferromagnetic L10 CrPt film as a pinning layer. dc magnetron sputtered [Pt/Cr] multilayers on a Co0.9Fe0.1 layer exhibit no exchange bias. After being annealed at 350 °C for 5 h in a vacuum, the equiatomic [Pt/Cr] multilayer stack is transformed into a uniform CrPt...

  • Flux pinning in Y[sub 1-x]Pr[sub x]Ba[sub 2]Cu[sub 3]O[sub 7-delta] high T[sub C] superconductors. Paulius, L.M.; Tsai, P.K. // Applied Physics Letters;4/22/1991, Vol. 58 Issue 16, p1792 

    Presents magnetic relaxation measurements on two sets of samples of high temperature superconductors. Fluxoid pinning potential; Effects of chemical doping on flux pinning; Mechanism for the enhancement of the fluxoid pinning potential; Magnetic relaxation for samples prepared by solid-state...

  • Flux pinning enhancement in melt-processed YBa2Cu3O7 with extended nanodefects. Shlyk, L.; Krabbes, G.; Fuchs, G.; Nenkov, K. // Applied Physics Letters;2/28/2005, Vol. 86 Issue 9, p092503 

    Melt-processed YBa2Cu3O7 (YBCO), containing a random array of Y–Ba–Cu–Ir–O nanostructures (about 20–150 nm in diameter and several μm in length) has been grown. The pinning efficiency of the resulting YBCO nanocomposite is superior to Li-doped or undoped...

  • Improved critical current densities in MgB2 tapes with ZrB2 doping. Zhang, Xianping; Gao, Zhaoshun; Wang, Dongliang; Yu, Zhengguang; Ma, Yanwei; Awaji, S.; Watanabe, K. // Applied Physics Letters;9/25/2006, Vol. 89 Issue 13, p132510 

    MgB2/Fe tapes with 2.5–15 at. % ZrB2 additions were prepared through the in situ powder-in-tube method. The phases, microstructures, critical current density, and flux pinning were characterized by means of x-ray diffraction, scanning electron microscope, and magnetic and transport...

  • Strong pinning enhancement in MgB2 using very small Dy2O3 additions. Chen, S. K.; Wei, M.; MacManus-Driscoll, J. L. // Applied Physics Letters;5/8/2006, Vol. 88 Issue 19, p192512 

    0.5–5.0 wt % Dy2O3 was in situ reacted with Mg+B to form pinned MgB2. While Tc remained largely unchanged, Jc was strongly enhanced. The best sample (only 0.5 wt % Dy2O3) had a Jc∼6.5×105 A cm-2 at 6 K, 1 T and 3.5×105 A cm-2 at 20 K, 1 T, around a factor of 4 higher compared...

  • Artificial domain wall nanotraps in Ni81Fe19 wires. Faulkner, Colm C.; Cooke, Michael D.; Allwood, Dan A.; Petit, Dorothée; Atkinson, Del; Cowburn, Russell P. // Journal of Applied Physics;6/1/2004, Vol. 95 Issue 11, p6717 

    We report on the controlled pinning and depinning of head-to-head domain walls with individual artificial nanotraps in rounded L-shaped Ni81Fe19 wires. Domain walls were nucleated and injected into one arm of an L-shaped planar wire structure with a wire width of 200 nm and a thickness of 5 nm....

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics