Electrochemical hydrogen permeation on steel sheets with in situ electrodeposition of a Pd layer at the exit side

Péter, L.; Szücs, E.; Filák, L.; Verö, B.; Schneider, H.
July 2003
Journal of Applied Electrochemistry;Jul2003, Vol. 33 Issue 7, p613
Academic Journal
Electrochemical hydrogen permeation experiments were performed on Ti-microalloyed steel sheets. The input side was polarized as a cathode in a solution containing H2SO4 and NaAsO2, while the solution at the exit side contained a concentrated NaOH solution with a minor amount of Pd(NO3)2. The presence of the palladium compound in the exit solution made it unnecessary to deposit an electrocatalytic Pd layer prior to the permeation experiments. Multistep permeation curves were recorded and the apparent diffusion coefficient of hydrogen, as calculated from the second breakthrough time, proved to be reproducible.


Related Articles

  • Electrodeposition of silver—tin alloys from pyrophosphate-cyanide electrolytes. Hrussanova, A.; Krastev, I. // Journal of Applied Electrochemistry;Jul2009, Vol. 39 Issue 7, p989 

    Using cyclic-voltammetric techniques, a pyrophosphate-cyanide electrolyte for the electrodeposition of compact Ag–Sn alloy coatings is investigated. This electrolyte is suited to further investigations on the alloy composition, structure and properties. The electrodeposition of coatings...

  • Electrodeposition of Au–Sn alloys from acid Au(III) baths. Bozzini, B.; Fanigliulo, A.; Giovannelli, G.; Natali, S.; Mele, C. // Journal of Applied Electrochemistry;Aug2003, Vol. 33 Issue 8, p747 

    A bath for the electrodeposition of white gold alloys of interest for the electroforming of hollow jewelry is proposed and investigated. The system was an acidic Au(III)–Sn(IV) bath for the electrodeposition of Au–Sn alloys. The electrochemical investigations were based on cyclic...

  • Influence of cobalt ions on the anodic oxidation of a lead alloy under conditions typical of copper electrowinning. Nguyen, T.; Guresin, N.; Nicol, M.; Atrens, A. // Journal of Applied Electrochemistry;Feb2008, Vol. 38 Issue 2, p215 

    The influence of cobalt ions in the solution on the anodic oxidation of a commercial Pb–Ca–Sn alloy under conditions typical of copper electrowinning was studied using cyclic voltammograms and potential decay transients. The cobalt ions changed the structure, morphology and...

  • Effect of nucleation mode on the morphology and texture of electrodeposited zinc. Raeissi, K.; Saatchi, A.; Golozar, M. A. // Journal of Applied Electrochemistry;Jul2003, Vol. 33 Issue 7, p635 

    The effect of temperature, pH and current density on the morphology and texture of electrodeposited zinc on mechanically polished steel was studied. The electrodeposited zinc had mostly basal (0 0 0 2) and low angle planes (1014, 1013, 1012) parallel to the surface. At pH 2, increasing...

  • Effect of benzylideneacetone on the electrodeposition mechanism of Zn–Co alloy. Trejo, G.; Ortega, R.; Meas, Y.; Chainet, E.; Ozil, P. // Journal of Applied Electrochemistry;May2003, Vol. 33 Issue 5, p373 

    The influence of benzylideneacetone (BA) on the mechanism of Zn–Co alloy electrodeposition onto AISI 1018 steel was studied in chloride acidic solutions. Results indicate that BA modifies the exchange current densities of zinc and cobalt such that the alloy is electrodeposited via a...

  • Kinetics of copper electrodeposition in the presence of triethyl-benzyl ammonium chloride. Varvara, S.; Muresan, L.; Popescu, I.C.; Maurin, G. // Journal of Applied Electrochemistry;Aug2003, Vol. 33 Issue 8, p685 

    Quasi-steady state hydrodynamic voltammetry at a rotating-disc electrode and electrochemical impedance spectroscopy were used to investigate the influence of triethyl-benzyl-ammonium (TEBA) chloride on the kinetics of copper electrodeposition from sulphate acidic electrolytes. SEM and X-ray...

  • Electrodeposition of FeCoNiCu nanowires. Huang, Q.; Davis, D.; Podlaha, E. J. // Journal of Applied Electrochemistry;Aug2006, Vol. 36 Issue 8, p871 

    Electrodeposition of FeCoNiCu/Cu nanometric, compositionally modulated alloy nanowires is presented. Pure Cu nanowires and Co-rich FeCoNiCu alloy nanowires were deposited from a single electrolyte. A double potential pulse scheme was used for multilayer deposition and significant anodic...

  • Comparison of the corrosion behaviour in 5% NaCl solution of Mg alloys NZ30K and AZ91D. Chang, J. W.; Peng, L. M.; Guo, X. W.; Atrens, A.; Fu, P. H.; Ding, W. J.; Wang, X. S. // Journal of Applied Electrochemistry;Feb2008, Vol. 38 Issue 2, p207 

    The corrosion behaviour of AZ91D and NZ30K (Mg–3Nd–0.2Zn–0.4Zr) alloys was investigated in 5% NaCl solution by immersion tests and electrochemical measurements. The immersion tests showed that the corrosion rate of NZ30K was about half that of AZ91D. The localized corrosion...

  • Mechanical plating 2. Wynn, Paul // Product Finishing;Apr2001, Vol. 54 Issue 4, p5 

    This series concludes with a review of process materials and performance benefits for this alternative system to electrodeposition and hot dip galvanizing. Additions of proprietary chemistry are made according to the total surface area of parts to be processed. They serve several functions in...


Read the Article


Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics