Analysis of Lattice Parameter Changes Following Deformation of a 0.19C-1.63Si-1.59Mn Transformation-Induced Plasticity Sheet Steel

Streicher-Clarke, A. M.; Speer, J. G.; Matlock, D. K.; DeCooman, B. C.; Williamson, D. L.
April 2005
Metallurgical & Materials Transactions. Part A;Apr2005, Vol. 36 Issue 4, p907
Academic Journal
Austenite and ferrite lattice parameters were monitored using X-ray diffraction subsequent to deformation in uniaxial and biaxial tension and plane straining of a 0.19C-1.63Si-1.59Mn transformation-induced plasticity (TRIP) sheet steel. Details from peak position results suggest the presence of stacking faults in the austenite phase, especially after deformation in uniaxial tension. The results also indicate residual stress or composition effects (through changes in the average carbon concentration due to selective transformation of lower carbon regions of austenite). Compressive residual stresses in the ferrite matrix were measured, and found to increase with increasing effective strain in specimens tested in biaxial tension and plane strain. Strain partitioning between softer ferrite and harder austenite (and possibly bainite or martensite) may be responsible for these residual compressive stresses in the ferrite, although volume expansion from the γ → α' transformation and texture gradients through the sheet thickness are also possible contributors.


Related Articles

  • In situ x-ray observation of bainitic transformation of austempered silicon alloyed steel. Xiang Chen; Vuorinen, Esa // Journal of Materials Research;Apr2009, Vol. 24 Issue 4, p30 

    The in situ x-ray diffraction observations of the bainitic transformation were conducted by using the high-temperature x-ray diffraction technique. The volume fraction and carbon content of austenite depend on the transformation temperature. The d{110} value of bainitic ferrite decreases with...

  • Determination of Stresses and Retained Austenite in Carbon Steels by X-rays - A Round Robin Study. Hosseini, S. B.; Karlsson, B.; Vuoristo, T.; Dalaei, K. // Experimental Mechanics;Jan2011, Vol. 51 Issue 1, p59 

    Residual stresses and retained austenite are two important process-related parameters which need to be controlled and monitored carefully during production and heat treatment of products. X-ray diffraction techniques are normally used in this context, and the purpose of the present study was to...

  • Welding induced residual stresses in explosion cladded AL-6XN superaustenitc stainless steel and ASME SA516-70 steel composite plates. Varavallo, Rogério; de Melo Moreira, Vitor; Paes, Vinicius; Brito, Pedro; Olivas, Jose; Pinto, Haroldo Cavalcanti // Advanced Materials Research;2014, Vol. 996, p451 

    Explosion welding is a solid state joining process that allows the manufacturing of corrosion resistant structural composite materials in the form of plates. In the present work, composite bimetal plates of AL-6XN superaustenitic stainless steel and ASME SA516-70 carbon steel produced by...

  • 'Finite element modeling of the effect of heat input on residual stresses in dissimilar joints'. Ranjbarnodeh, Eslam; Serajzadeh, Siamak; Hosein Kokabi, Amir; Hanke, Stefanie; Fischer, Alfons // International Journal of Advanced Manufacturing Technology;Jul2011, Vol. 55 Issue 5-8, p649 

    In the present study, a thermo-elastic-plastic model was developed in order to evaluate the residual stresses in dissimilar automatic tungsten inert gas (TIG) welds between plain carbon steel CK4 and a ferritic stainless steel AISI409. The effect of welding heat input on the magnitude and the...

  • Investigations of residual stress distributions in retained austenite and martensite after carbonitriding of a low alloy steel. Katemi, Richard J.; Epp, Jérémy; Hoffmann, Franz; Steinbacher, Matthias // Advanced Materials Research;2014, Vol. 996, p550 

    Specimens of low alloy steel were carbonitrided under different conditions to attain varying levels of carbon and nitrogen contents. The residual stress depth distribution was evaluated in martensite and retained austenite by X-ray diffraction. Beside standard evaluations, triaxial residual...

  • Evaluation of Welding Residual Stresses Using Diffraction Spot Trace Method. Kenji Suzuki; Takahisa Shobu; Ayumi Shiro; Shuoyuan Zhang // Advanced Materials Research;2014, Vol. 996, p76 

    A diffraction spot trace method (DSTM) is very useful to measure internal stresses of materials with coarse grains. In this study, validity of the DSTM was examined using high energy synchrotron X-rays of 70 keV. The specimen was a welded plate of austenitic stainless steel (SUS316L). The...

  • External reference samples for residual stress analysis by X-ray diffraction. Lefebvre, F.; Wasniewski, E.; Francois, M.; Cacot, J.; Le-bec, P.; Baumhauer, E.; Bouscaud, D.; Bergey, T.; Blaize, D.; Gloaguen, D.; Cosson, A.; Jegou, S.; Cheynet, Y.; Leray, S.; Meheux, M.; Monvoisin, J. C.; Allain, P.; Vidal, J. C.; Sprauel, J. M.; Goudeau, P. // Advanced Materials Research;2014, Vol. 996, p221 

    The GFAC (French Association for residual stress analysis) has been working for several years on external reference samples in relation with the EN 15305-2009 standard. The purpose of this campaign is to provide an external reference sample to each laboratory involved in the round-robin to allow...

  • Mapping Multiple Components of the Residual Stress Tensor in a Large P91 Steel Pipe Girth Weld Using a Single Contour Cut. Hosseinzadeh, F.; Bouchard, P. // Experimental Mechanics;Feb2013, Vol. 53 Issue 2, p171 

    The contour method is applied in an innovative manner to measure the distribution of hoop residual stress in a large martensitic-ferritic steel pipe containing a multi-pass girth weld. First, a novel one-step wire electro-discharge machining cut is conducted to divide the pipe lengthways into...

  • NON-CONTACT ACOUSTO-THERMAL SIGNATURES OF PLASTIC DEFORMATION IN TI-6AL-4V. Welter, J. T.; Malott, G.; Schehl, N.; Sathish, S.; Jata, K. V.; Blodgett, M. P. // AIP Conference Proceedings;2/22/2010, Vol. 1211 Issue 1, p1397 

    Plastic deformation introduces changes in a material which include increases in: dislocations, strains, residual stress, and yield stress. However, these changes have a very small impact on the material properties such as elastic modulus, conductivity and ultrasonic wave speed. This is due to...


Read the Article


Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics