TITLE

A low external temperature method for synthesis of active electrode materials for Li batteries - Part A: Synthesis of pure manganese spinel

AUTHOR(S)
Uzunova, S.; Banov, B.; Momchilov, A.; Vassilev, S.; Stankulov, T.; Uzunov, I.
PUB. DATE
February 2005
SOURCE
Journal of Applied Electrochemistry;Feb2005, Vol. 35 Issue 2, p117
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
A low external temperature method (LETM) of active electrode material synthesis for lithium ion batteries has been proposed. The method consists of a two-step process, which is comprised of drying fine droplets of a solution of the starting compound in a liquid drying agent at 200?°C, followed by calcination of the obtained precursor in a fluidised bed at a furnace temperature of 300?°C. The method prevents uncontrolled growth of particles during the initial thermal pre-treatment and the final firing process. Lithium manganese spinel has been selected for describing the proposed LETM of synthesis. The properties of the spinel obtained by LETM are compared with those of a spinel obtained by the classical immobilised solid state synthesis at 750 °C. On electrochemical cycling, the capacity loss after 100 cycles of the LETM spinel at 11% is significantly lower than that for the spinel prepared by solid state methods (21.5%). However, only 3% difference is seen in the total integral capacity over the 100 cycles between spinels prepared by the different methods.
ACCESSION #
16212753

 

Related Articles

  • Modelling improves Li ions.  // Electronics Weekly;2/22/2006, Issue 2229, p10 

    This article reports that researchers in the U.S. have used computer modelling to improve the charge and discharge rate of a lithium battery electrode material. The models revealed changes to the crystal structure of lithium nickel manganese oxide. The researchers, from MIT and the State...

  • New window into problems with lithium batteries. Ford, Jason // Engineer (Online Edition);10/20/2016, p1 

    The article reports that researchers at the University of Michigan have observed a phenomenon that can be problematic to next-generation lithium batteries.

  • LiMn2-xNixO4 Spinel Oxides as High-Temperature Lithium Battery Cathode Materials for Borehole Applications. Zhenjie Wang; Junlin Du; Weiyuan Duan; Yongqiang Niu; Zhu Wu // International Journal of Electrochemical Science;May2013, Vol. 8 Issue 5, p6231 

    LiMn2-xNixO4 and its Ni-substituted derivative electrodes are successfully introduced to high-temperature lithium batteries for borehole applications. The samples prepared by a sol-gel method each have a single spinel-phase, small particle size of 100-200 nm, and excellent discharge capacity....

  • Progress in Li-air battery technology.  // Industrial Ceramics;Dec2009, Vol. 29 Issue 3, p205 

    The article reports on the lithium-air cell with solid conductor glass film developed by researchers at the National Institute of Advanced Industrial Science and Technology (AIST) in Japan, which separates electrolytes and avoids solid products from forming and clogging the electrode.

  • Hydrolytic Lignin: It’s Activated and Fluorinated Forms. Nikolenko, Yury; Tsvetnikov, Aleksander; Ustinov, Aleksander; Silant’ev, Vladimir; Kuryavyi, Valery; Ziatdinov, Albert // Key Engineering Materials;2019, Vol. 806, p100 

    The hydrolytic lignin (HL) derivatives have been prepared via its physical activation (high-temperature annealing in vacuum) followed by chemical modification (fluorination). It was found that the graphitized product of thermal activation up to 1000 °C at a low temperature gain rate of < 2...

  • Investigation on the root cause of the decreased performances in the overcharged lithium iron phosphate battery. Zhang, Jiangyun; Yang, Xiaoqing; Zhang, Guoqing; Huang, Qiqiu; Xiao, Changren; Yang, Chuxiong // International Journal of Energy Research;Jun2018, Vol. 42 Issue 7, p2448 

    Summary: The overcharge of the lithium iron phosphate (LiFePO4) batteries usually leads to the sharp capacity fading and safety issues, especially under low temperature environment. Thus, investigating their root cause originated from the electrode materials is critical for the safety...

  • Electrochemical performance of modified synthetic graphite for lithium ion batteries. Jung-Kyun Baek; Heon-Young Lee; Serk-Won Jang; Sung-Man Lee // Journal of Materials Science;Jan2005, Vol. 40 Issue 2, p347 

    The carbon-coated composite has been manufactured and investigated as the negative electrode for Li-ion batteries. The carbon-coated composite powders are prepared by a simple mixing of two types of synthetic graphite particles (SFG6 and SFG44) with polyvinylchloride powders and heating to a...

  • Electrochemical properties of nanosize Sn-coated graphite anodes in lithium-ion cells. Wang, G.X.; Yao, Jane; Ahn, Jung-Ho; Liu, H.K.; Dou, S.X. // Journal of Applied Electrochemistry;Feb2004, Vol. 34 Issue 2, p187 

    A series of Sn-coated graphite composite materials for lithium-ion batteries were prepared by microencapsulating nanosize Sn particles in graphite. The nanosize Sn particles are homogeneously dispersed in the graphite matrix via electroless chemical reduction. The tin-graphite composite showed a...

  • Low temperature performance of graphite and LiNiCoMnO electrodes in Li-ion batteries. Yaqub, Adnan; Lee, You-Jin; Hwang, Min; Pervez, Syed; Farooq, Umer; Choi, Jeong-Hee; Kim, Doohun; Choi, Hae-Young; Cho, Seong-Back; Doh, Chil-Hoon // Journal of Materials Science;Nov2014, Vol. 49 Issue 22, p7707 

    Low temperature (LT) behavior of graphite/LiNiCoMnO (NCM622) cells prepared with low loading or LL (thinner electrodes prepared with low loading and packing density) and high loading or HL (thicker electrodes prepared with high loading and packing density) were investigated. The cells were...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics