TITLE

Magnetoelectric interactions in hot-pressed nickel zinc ferrite and lead zirconante titanate composites

AUTHOR(S)
Srinivasan, G.; DeVreugd, C. P.; Flattery, C. S.; Laletsin, V. M.; Paddubnaya, N.
PUB. DATE
September 2004
SOURCE
Applied Physics Letters;9/27/2004, Vol. 85 Issue 13, p2550
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
The synthesis by hot pressing and wide-band (10Hz-1 MHz) magnetoelectric (ME) characterization of bulk composites of nickel zinc ferrite Ni1-xZnxFe2O4 (NZFO) (x=0-0.5) and lead zirconate titanate (PZT) are reported. Hot-pressed samples show an order of magnitude improvement in ME voltage coefficient compared to sintered samples. Frequency dependence of ME coefficients show a three order of magnitude enhancement at electromechanical resonance. The ME coupling is maximum for samples with equal volume of ferrite and PZT. The strongest ME interactions are measured for samples of NZFO (x=0.2) and PZT.
ACCESSION #
14546605

 

Related Articles

  • Ultralow-frequency magnetoelectric effect in a multilayer ferrite-piezoelectric structure. Kamentsev, K.; Fetisov, Y.; Srinivasan, G. // Technical Physics;Jun2007, Vol. 52 Issue 6, p727 

    The magnetoelectric effect is experimentally studied in a multilayer nickel zinc ferrite-lead zirconate titanate structure at frequencies of 10−3–10 Hz that is placed in a harmonically modulated magnetic field of amplitude to 1 kOe. The nonlinearity of the ferrite magnetostriction...

  • Microscopic magnetic squeezer. Helseth, L. E.; Fischer, T. M.; Hansen, R. W.; Johansen, T. H. // Applied Physics Letters;9/27/2004, Vol. 85 Issue 13, p2556 

    A microscopic magnetic squeezer based oil two magnetic domain walls moving along a one-dimensional potential well generated by a stress line in ferrite garnet films is demonstrated. The squeezer can operate on magnetic objects of size 1–200 μm and exert compressive forces up to 10 pN....

  • On the Magnetic Field Acting upon Moving Domain Walls in (Bi,Yb)[sub 3](Fe,Ga)[sub 5]O[sub 12] Garnet Ferrite Films. Randoshkin, V. V.; Polezhaev, V. A.; Sazhin, Yu. N.; Sysoev, N. N.; Dudorov, V. N. // Technical Physics Letters;Jul2002, Vol. 28 Issue 7, p595 

    The dependence of the domain wall velocity V on the magnetic field strength H in (111)-oriented (Bi,Yb)[sub 3](Fe,Ga)[sub 5]O[sub 12] single crystal garnet ferrite films is studied by the method of pulsed remagnetization at the point of angular momentum compensation. It is established that the...

  • Magnetoelectric nano-Fe3O4/CoFe2O4∥PbZr0.53Ti0.47O3 composite. Shenqiang Ren; Wuttig, Manfred // Applied Physics Letters;2/25/2008, Vol. 92 Issue 8, p083502 

    A new magnetoelectric hybrid device composed of a nanoparticulate magnetostrictive iron oxide-cobalt ferrite film on a piezoelectric lead zirconic titanate crystal serving as both substrate and straining medium is described. Nano-Fe3O4/CoFe2O4 particles, ranging from 5 to 42 nm, were prepared...

  • Cigar-shaped ferrite nanocrystals: Orientation of the easy magnetic axes. Ngo, A. T.; Pileni, M. P. // Journal of Applied Physics;10/15/2002, Vol. 92 Issue 8, p4649 

    Mesoscopic structures made of cigar-shaped γ-Fe[SUB2]O[SUB3] nanocrystals with an average length of 325 nm and aspect ratio of 7 are described. The structures were prepared starting from an aqueous solution to which a magnetic field parallel to the substrate could be applied during the...

  • Does Ti+4 Ratio Improve the Physical Properties of CdxCo1-x+tTitFe2-2tO4? Ahmed, M. A.; Mansour, S. F.; El-Dek, S. I. // AIP Conference Proceedings;2007, Vol. 888 Issue 1, p122 

    The microstructure and magnetic properties of Ti substituted CoCd ferrites of the general formula CdxCo1-x+tTitFe2-2tO4, x = 0.20, 0.00<=t<=0.25 have been reported. The ferrite samples were prepared by standard double sintering ceramic technique and structural analysis was carried out using...

  • Classical Dependence of the Domain Wall Velocity on the Magnetic Field in Garnet Ferrite Films with Orthorhombic Magnetic Anisotropy. Randoshkin, V. V.; Sazhin, Yu. N. // Physics of the Solid State;May2002, Vol. 44 Issue 5, p893 

    The dependence of the domain wall velocity V on the acting magnetic field H is investigated for bismuth-containing single-crystal garnet ferrite films with orthorhombic magnetic anisotropy. It is shown that this dependence includes both the initial linear portion and a saturation portion and...

  • Spontaneous magnetization generated by spin, pulsating, and planar combustion synthesis. Martirosyan, K. S.; Claycomb, J. R.; Gogoshin, G.; Yarbrough, R. A.; Miller, J. H.; Luss, D. // Journal of Applied Physics;6/1/2003, Vol. 93 Issue 11, p9329 

    The motion of the high temperature front during combustion synthesis of ferrite materials generates residual magnetization in cylindrical product samples. The combustion wave created a current density of up to 10 A/cm[sup 2], which influenced the magnetization distribution. The measured peak...

  • Magnetic micromachines prepared by ferrite plating technique. Nishimura, K.; Uchida, H.; Inoue, M.; Sendoh, M.; Ishiyama, K.; Arai, K. I. // Journal of Applied Physics;5/15/2003, Vol. 93 Issue 10, p6712 

    By the sterolithography technique and the ferrite plating, we fabricated three types of magnetic micromachines which coated Fe[SUB3]O[SUB4], Co[SUB0.39]Fe[SUB2.61]O[SUB4], and Co[SUB0.45]Fe[SUB2.55]O[SUB4], respectively. The stereolithography technique enables one to form the spiral-shape...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics