Highly processable bulk metallic glass-forming alloys in the Pt–Co–Ni–Cu–P system

Schroers, Jan; Johnson, William L.
May 2004
Applied Physics Letters;5/3/2004, Vol. 84 Issue 18, p3666
Academic Journal
Highly processable bulk metallic glass alloys in the Pt–Co–Ni–Cu–P system were discovered. The alloys show low liquidus temperature below 900 K, excellent processability with low critical cooling rate reflecting in maximum casting thicknesses in quartz tubes of up to 20 mm, and a large supercooled liquid region. The Pt57.5Cu14.7Ni5.3P22.5 composition has a liquidus temperature of 795 K, a glass transition temperature of 508 K with a supercooled liquid region of 98 K. For medical and jewelry applications a Ni-free alloy, Pt60Cu16Co2P22 was discovered with a liquidus temperature of 881 K, a glass transition temperature of 506 K, and a supercooled liquid region of 63 K. Glass formation was observed in a wider composition range. Vickers hardness of these alloys is in the 400 Hv range. The alloys can be processed in the supercooled liquid region in air without any measurable oxidation. In this region, a large processing window is available in which the material does not embrittle. Embrittlement in these alloys is correlated with crystallization. It can be avoided as long as substantial crystallization does not take place during isothermal processing in the supercooled liquid region. Also, liquid processing can be performed in air when flux with B2O3. © 2004 American Institute of Physics.


Related Articles

  • Magnetic Relaxations in Amorphous Fe61Co10Y8Zr1B20 Alloy. PIETRUSIEWICZ, P.; BŁOCH, K.; GONDRO, J.; NABIAŁEK, M.; DOŠPIAŁ, M.; SZOTA, M. // Acta Physica Polonica, A.;Jun2014, Vol. 125 Issue 6, p106 

    Effects of annealing on the disaccommodation phenomenon in bulk metallic glasses (BMGs), obtained by injection-casting method have been studied. The amorphous structure has been confirmed using X-ray diffractometer. The annealing process has been performed at temperature below the...

  • Role of minor alloying additions in formation of bulk metallic glasses: A Review. Lu, Z. P.; Liu, C. T. // Journal of Materials Science;Jun2004, Vol. 39 Issue 12, p3965 

    Minor alloying addition or microalloying technology has already shown dramatic effects on glass formation and thermal stability of bulk metallic glasses (BMGs). This paper intends to provide a comprehensive review of recent developments of this technology in the field of BMGs. The beneficial...

  • Prediction of Glass-Forming Compositions in Metallic Systems: Copper-Based Bulk Metallic Glasses in the Cu-Mg-Ca System. Laws, Kevin J.; Shamlaye, Karl F.; Wong, Kenneth; Gun, Bulent; Ferry, Michael // Metallurgical & Materials Transactions. Part A;Jul2010, Vol. 41 Issue 7, p1699 

    A novel methodology for predicting specific compositions for glass-forming alloys based on efficiently packed atomic cluster selection, liquidus lines, and ab initio calculations is presented. This model has shown applicable adaptation to many known metallic and ceramic oxide glass-forming...

  • Mechanically driven phase separation and corresponding microhardness change in Cu60Zr20Ti20 bulk metallic glass. Qingping Cao; Jinfi Li; Yaohe Zhou; Jianzhong Jiang // Applied Physics Letters;2/21/2005, Vol. 86 Issue 8, p081913 

    Rolling deformation of bulk Cu60Zr20Ti20 metallic glass has been performed at cryogenic temperature. The specimens exhibit excellent ductility, and are rolled up to 97% reduction in thickness without fracture. Crystallization is suppressed during the deformation, however, phase separation is...

  • Glass-forming ability enhanced by proper additions of oxygen in a Fe-based bulk metallic glass. Li, H. X.; Gao, J. E.; Jiao, Z. B.; Wu, Y.; Lu, Z. P. // Applied Physics Letters;10/19/2009, Vol. 95 Issue 16, p161905 

    Effects of oxygen on glass formation in the Fe73Mo3.0C7.0Si3.3B5.0P8.7 bulk metallic glass were studied in detail. Surprisingly, it was found that a critical level of oxygen is effective in enhancing the glass-forming ability of the current Fe-based bulk metallic glass due to the facts that (i)...

  • Modified efficient cluster packing model for calculating alloy compositions with high glass forming ability. Wang, A. P.; Wang, J. Q.; Ma, E. // Applied Physics Letters;3/19/2007, Vol. 90 Issue 12, p121912 

    The efficient cluster packing model for bulk metallic glasses (BMGs) has been modified and extended to allow quantitative predictions of alloy compositions with high glass forming ability. The compositions calculated using this simple method compare favorably with the vast majority of the BMGs...

  • Contributions to the homogeneous plastic flow of in situ metallic glass matrix composites. Fu, X. L.; Li, Y.; Schuh, C. A. // Applied Physics Letters;12/12/2005, Vol. 87 Issue 24, p241904 

    The homogeneous deformation of Zr-based bulk metallic glass composites is studied near the glass transition temperature, at various levels of reinforcement volume fraction. Through examination of the constitutive response, it is seen that the presence of in situ reinforcements increases the flow...

  • Ni-based bulk glassy alloys with superhigh strength of 3800 MPa in Ni–Fe–B–Si–Nb system. Baolong Shen; Chuntao Chang; Inoue, Akihisa // Applied Physics Letters;5/15/2006, Vol. 88 Issue 20, p201903 

    The effects of replacement of Ni by Fe on the glass-forming ability (GFA) and mechanical properties of Ni–B–Si–Nb glassy alloys were examined. The substitution of Fe for Ni caused increases of GFA and mechanical properties. Ni-based bulk glassy alloys (BGAs) with diameters...

  • Binary eutectic clusters and glass formation in ideal glass-forming liquids. Lu, Z. P.; Shen, J.; Xing, D. W.; Sun, J. F.; Liu, C. T. // Applied Physics Letters;8/14/2006, Vol. 89 Issue 7, p071910 

    In this letter, a physical concept of binary eutectic clusters in “ideal” glass-forming liquids is proposed based on the characteristics of most well-known bulk metallic glasses (BMGs). The authors approach also includes the treatment of binary eutectic clusters as basic units, which...


Read the Article


Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics