TITLE

X-ray Diffraction Analysis of ProRoot Mineral Trioxide Aggregate Hydrated at Different pH Values

AUTHOR(S)
Akhavan, Hengameh; Mohebbi, Pooneh; Firouzi, Amir; Noroozi, Mehdi
PUB. DATE
March 2016
SOURCE
Iranian Endodontic Journal;Spring2016, Vol. 11 Issue 2, p111
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
Introduction: The aim of this study was to compare the chemical compounds of white ProRoot mineral trioxide aggregate (WMTA) hydrated at different pH environments. Methods and Materials: Mixed samples of WMTA were kept in acidic (pH=5.4), neutral (pH=7.4) and alkaline (pH=9.4) environments for 48 h. Then, X-ray diffraction (XRD) analysis was performed for both hydrated and powder forms of WMTA. Portlandite crystalline structures of environments were compared from three aspects: intensity (height of the peak, corresponding to the concentration), crystallinity (peak area/total area) and crystal size (full-width at half-maximum of the peak). Results: After matching the peaks of each sample with those of the International Center for Diffraction Data (ICDD) database, the main constituent of all set cements and powder form was found to be bismuth oxide. Acidic environment exhibited lower intensity and crystallinity of portlandite in comparison with neutral environment. Conclusion: The highest concentration and crystallinity of portlandite were observed in WMTA samples hydrated at neutral pH and the highest crystal size was detected after hydration in alkaline pH.
ACCESSION #
114525677

 

Related Articles

  • The Chemo-Physical and Biological Properties of Portland Cement/Bismuth Oxide/Zinc Oxide Composites Hydrated by a Novel Calcium Lactate Gluconate (CLG) Accelerant. Teng, Nai-Chia; Hsieh, Sung-Chih; Chen, Chien-Chung; Ke, En-Sheng; Ji, Dian-Yu; Cheng, Shu-Lien; Yang, Jen-Chang // Current Nutrition & Food Science;Apr2014, Vol. 10 Issue 2, p217 

    This objective of this study is to investigate the antibacterial properties and biocompatibility of Portland cement/bismuth oxide/ zinc oxide (PC/Bi2O3/ZnO) composites hydrated by a novel calcium lactate gluconate (CLG) accelerant. The 23.1 wt% CLG aqueous solution and deionized water (DDW) were...

  • The Effect of pH on Surface Hardness of Mineral Trioxide Aggregate with Various Additives. Mohan, Nimisha; Mishra, Lora; Ravishanker P.; Subba rao, C. V. // Internet Journal of Dental Science;2010, Vol. 8 Issue 2, p3 

    Background and Aim:To evaluate the surface microhardness of mineral trioxide aggregate (MTA) mixed with various additives after exposure of their surface to acidic pH during hydration.Materials and Methods: White ProRoot MTA was mixed with various additives like saline, lidocaine, 2% calcium...

  • THE EFFECT OF PH ON SURFACE HARDNESS OF MINERAL TRIOXIDE AGGREGATE WITH VARIOUS ADDITIVES. Mohan, Nimisha; Mishra, Lora; Subba rao, C. V. // Romanian Journal of Stomatology;2010, Vol. 56 Issue 3, p222 

    Background and Aim: To evaluate the surface microhardness of mineral trioxide aggregate (MTA) mixed with various additives after exposure of their surface to acidic pH during hydration. Materials and Methods: White ProRoot MTA was mixed with various additives like saline, lidocaine, 2% calcium...

  • Effect of Tricalcium Aluminate on the Physicochemical Properties, Bioactivity, and Biocompatibility of Partially Stabilized Cements. Chang, Kai-Chun; Chang, Chia-Chieh; Huang, Ying-Chieh; Chen, Min-Hua; Lin, Feng-Huei; Lin, Chun-Pin // PLoS ONE;Sep2014, Vol. 9 Issue 9, p1 

    Background/Purpose: Mineral Trioxide Aggregate (MTA) was widely used as a root-end filling material and for vital pulp therapy. A significant disadvantage to MTA is the prolonged setting time has limited the application in endodontic treatments. This study examined the physicochemical...

  • Push-Out Bond Strength and Surface Microhardness of Calcium Silicate-Based Biomaterials: An in vitro Study. Majeed, Abdul; AlShwaimi, Emad // Medical Principles & Practice;Mar2017, Vol. 26 Issue 2, p139 

    Objective: This was an in vitro evaluation of push-out bond strength and surface microhardness of calcium silicate-based biomaterials in coronal and apical root dentin.Materials and Methods: Ninety sections (2 mm thick) of coronal and apical root dentin were obtained...

  • Effect of Acidic Environment on Dislocation Resistance of Endosequence Root Repair Material and Mineral Trioxide Aggregate. Shokouhinejad, Noushin; Ashofteh Yazdi, Kazem; Hossein Nekoofar, Mohammad; Matmir, Shakiba; Khoshkhounejad, Mehrfam // Journal of Dentistry of Tehran University of Medical Sciences;Mar2014, Vol. 11 Issue 2, p161 

    Objective: The aim of this study was to compare the effect of an acidic environment on dislocation resistance (push-out bond strength) of EndoSequence Root Repair Material (ERRM putty and ERRM paste), a new bioceramic-based material, to that of mineral tri-oxide aggregate (MTA). Materials and...

  • Effect of CaCl2 on Chemical Properties of Mineral Trioxide Aggregate. Stavileci, Miranda; Hoxha, Veton; Kamberi, Blerim; Vula, Violeta; Bajrami, Donika; Kameri, Ariana // Acta Stomatologica Croatica;2008, Vol. 42 Issue 2, p171 

    MTA has been proposed for various treatment alternatives due to its high biocompatibility. However delayed setting times may limit its use. Objectives: The aim of this study was to evaluate the effect of adding a setting accelerator 5% or 10% CaCl2 to MTA on the pH and calcium ion release of MTA...

  • An In vitro Comparison of Furcal Perforation Repaired with Pro-root MTA and New Endodontic Cement in Primary Molar Teeth- A Microleakage Study. R., Haghgoo; M., Niyakan; K., Nazari Moghaddam; S., Asgary; N, Mostafaloo // Journal of Dentistry (17283426);Mar2014, Vol. 15 Issue 1, p28 

    The article investigates the furcal perforation of primary molar teeth which is repaired using the pro-root mineral trioxide aggregate (MTA) and new endodontic cement (NEC). Two layers of resin composite were used to seal the orifes and the root apices of the extracted primary molars. The teeth...

  • The effect of blood contamination on dislocation resistance of different endodontic reparative materials. Üstün, Yakup; Topçuoğlu, Hüseyin S.; Akpek, Firdevs; Aslan, Tuğrul; S Topçuoğlu, Hüseyin // Journal of Oral Science;Sep2015, Vol. 57 Issue 3, p185 

    This study evaluated the retention characteristics of ProRoot mineral trioxide aggregate (MTA), RetroMTA, Supra MTA, and Biodentine biomaterials used to repair furcation perforations contaminated with blood. Furcal perforations measuring 1.3 mm in diameter and 2 mm in height were created in 96...

  • Placement in an acidic environment increase the solubility of white mineral trioxide aggregate. Reza Yavari, Hamid; Borna, Zahra; Rahimi, Saeed; Shahi, Shahriar; Valizadeh, Hadi; Ghojazadeh, Morteza // Journal of Conservative Dentistry;May/Jun2013, Vol. 16 Issue 3, p257 

    Aims: The aim of the present study was to evaluate solubility of white mineral trioxide aggregate (WMTA) in an acidic environment. Materials and Methods: Twenty-four metal rings were prepared, filled with WMTA and randomly divided into two groups. The samples in groups 1 and 2 were set in...

Share

Read the Article

Courtesy of THE LIBRARY OF VIRGINIA

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics