TITLE

Effect of Al doping in GaN films grown by metalorganic chemical vapor deposition

AUTHOR(S)
Lee, Jae-Hoon; Hahm, Sung-Ho; Lee, Jung-Hee; Bae, Sung-Bum; Lee, Kyu-Seok; Cho, Yong-Hoon; Lee, Jong-Lam
PUB. DATE
August 2003
SOURCE
Applied Physics Letters;8/4/2003, Vol. 83 Issue 5, p917
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
The effect of Al doping in GaN films grown by metalorganic chemical vapor deposition was investigated using photoluminescence (PL), time-resolved PL, Hall measurements, and reciprocal space map. The electron mobility measured at 300 (150) K by a Hall measurement significantly increased from 170 (185) cm[SUP2]/V s in the undoped sample to 524 (744) cm[SUP2]/V s in the Al-doped sample grown with a molar flow rate ratio Al/(Al1Ga) of 0.056. When increasing the incorporation of Al in GaN, the band edge photoluminescence emission intensity was enhanced by about one order of magnitude compared to the undoped GaN. In addition, an increase in the decay lifetime of the GaN band edge emission was observed with the Al-doped GaN. In conclusion, the incorporation of only a small amount of Al in GaN was found to significantly reduce the point-defect-related electron scattering center associated with the compensating acceptors (Ga vacancies or their complexes) and nonradiative recombination centers, thereby improving the electrical and optical properties of GaN films.
ACCESSION #
10404925

 

Related Articles

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics