Photostimulated luminescence in Eu-doped fluorochlorozirconate glass ceramics

AUTHOR(S)
Schweizer, Stefan; Hobbs, Linn W.; Secu, Mihail; Spaeth, Johann-Martin; Edgar, Andrew; Williams, Grant V. M.
PUB. DATE
July 2003
SOURCE
Applied Physics Letters;7/21/2003, Vol. 83 Issue 3, p449
SOURCE TYPE
Academic Journal
DOC. TYPE
Article
ABSTRACT
We report the synthesis of Eu[SUP2+]- and chlorine-doped fluorozirconate glass-ceramics that show an intense photostimulated luminescence (PSL) after x-ray irradiation at room temperature. The PSL efficiency is up to 80% of that found in the well-known crystalline x-ray storage phosphor BaFBr:Eu[SUP2+], and it is the largest thus far reported for a glass-ceramic. We attribute the PSL to crystallites of orthorhombic BaCl[SUB2] that are formed after annealing above the glass temperature. Hexagonal BaCl[SUB2] crystallites are also observed after short annealing times, but they do not provide a measurable PSL signal. The photoluminescence peak from glass-ceramics containing orthorhombic BaCl[SUB2] crystallites occurs at 402 nm, and the stimulation band is centered at about 560 nm.
ACCESSION #
10281616

 

Related Articles

  • Temperature-dependent broadband near-infrared luminescence in silicate glass ceramics containing Li2MgSiO2: Cr4+ nanocrystals. Yixi Zhuang; Jiajia Zhou; Junhua Xie; Yu Teng; Jianrong Qiu // Journal of Materials Research;Sep2010, Vol. 25 Issue 9, p1833 

    Transparent glass ceramics containing Li2MgSiO4: Cr4+ nanocrystallites were prepared. Intense broadband near-infrared emission with full width at half-maximum larger than 200 nm and long fluorescence lifetime (t > 100 µs) were observed. The temperature-dependent optical characteristics of the...

  • Synthesis and luminescence of fluorochloride glasses activated by Er3+. Brekhovskikh, M. N.; Galagan, B. I.; Dmitruk, L. N.; Moiseeva, L. V.; Fedorov, V. A. // Inorganic Materials;May2009, Vol. 45 Issue 5, p579 

    Fluorochloride glasses activated by Er3+ and glass ceramics of 57HfF4 · 20BaCl2 · 3LaF3 · 3InF3 · 17NaF composition were synthesized. For the given glasses, Er3+ luminescence in the region of 1.55 μm was studied in comparison with fluoride glasses and glass ceramics of similar...

  • Broadband optical amplification in silicate glass ceramics containing Li2ZnSiO4:Cr4+ nanocrystals. Yixi Zhuang; Yu Teng; Jin Luo; Bin Zhu; Yingzhi Chi; Wu, E.; Heping Zeng; Jianrong Qiu // Applied Physics Letters;9/14/2009, Vol. 95 Issue 11, p111913 

    Transparent glass ceramics containing Li2ZnSiO4:Cr4+ nanocrystals are prepared and their optical properties are investigated. The glass ceramics show intense broadband infrared luminescence and long fluorescence lifetime of about 90 μs. The single-pass optical amplification is demonstrated on...

  • Broadband near-infrared emission from transparent Ni2+-doped silicate glass ceramics. Zhou, Shifeng; Dong, Huafang; Zeng, Heping; Wu, Botao; Zhu, Bin; Yang, Hucheng; Xu, Shiqing; Wan, Zhiyu; Qiu, Jianrong // Journal of Applied Physics;Sep2007, Vol. 102 Issue 6, p063106 

    Transparent Ni2+-doped MgO–Al2O3–TiO2–SiO2 glass ceramics were prepared, and the optical properties of Ni2+-doped glass ceramics were investigated. Broadband emission centered at 1320 nm was observed by 980 nm excitation. The longer wavelength luminescence compared with...

  • New High-Brightness Long-Lasting Phosphorescent Glass-Ceramic. Baoshan Feng; Jinchao Zhang; Li Song; Xiangyang Yu // American Ceramic Society Bulletin;Jan2008, Vol. 87 Issue 1, p53 

    The article introduces a new semi-transparent and high-brightness long-lasting phosphorescent (LLP) glass-ceramic. The LLPs are a type of phosphors that have a long, persistent afterglow emission. The author discusses the preparations done for LLP. The characteristics of the new LLP are also...

  • Up- and Downconversion Luminescence Properties of Nd3+ Ions Doped in Bi2O3-BaO-B2O3 Glass System. Ruamnikhom, R.; Limsuwan, P.; Horprathum, M.; Chanthima, N.; Kim, H. J.; Ruengsri, S.; Kaewkhao, J. // Advances in Materials Science & Engineering;2014, p1 

    Physical, optical, and luminescence properties of Nd3+ ions in bismuth barium borate glass system were studied. The glasses prepared by a melt quenching method were doped at various Nd2O3 concentrations in compositions (40-x)B2O3 : 40Bi2O3 : 20BaO : xNd2O3 (where x = 0.00, 0.50, 1.00, 1.50,...

  • LaF3 nanocrystals as a host for Er3+ in oxyfluoride glass. Środa, Marcin; Reben, Manuela; Kwaśny, Mirosław; Wacławska, Irena // Optica Applicata;2005, Vol. 35 Issue 4, p851 

    The paper presents new glass-ceramics as a material for up-conversion luminescence. Formation of the LaF3 nanocrystals have been obtained as a low phonon host for rare earth active ions in oxide glassy matrix. The thermal conditions of LaF3 nanocrystallization in the glass from the...

  • Near-infrared luminescence of rare earth ions in oxyfluoride lead borate glasses and transparent glass-ceramic materials. PISARSKA, JOANNA; RYBA-ROMANOWSKI, WITOLD; DOMINIAK-DZIK, GRAŻYNA; GORYCZKA, TOMASZ; PISARSKI, WOJCIECH A. // Optica Applicata;2008, Vol. 38 Issue 1, p211 

    Oxyfluoride lead borate glasses singly doped with Nd3+ and Er3+ ions have been studied before and after thermal treatment. The orthorhombic PbF2 crystallites are formed during thermal treatment, which was evidenced by X-ray diffraction analysis. Near-infrared luminescence spectra at 1.06 µm...

  • Enhancement of photoluminescence intensity by photoinduced interdiffusion in nanolayered a-Se/As2S3 films. Adarsh, K. V.; Sangunni, K. S.; Kokenyesi, S.; Ivan, I.; Shipljak, M. // Journal of Applied Physics;2/15/2005, Vol. 97 Issue 4, p044314 

    Optical parameters of chalcogenide glass multilayers with 12–15 nm modulation lengths prepared by thermal evaporation can be changed by laser irradiation. Photoluminescence (PL) studies were carried out on such nonirradiated and irradiated multilayered samples of a-Se/As2S3 (sublayer...

Share

Read the Article

Courtesy of VIRGINIA BEACH PUBLIC LIBRARY AND SYSTEM

Sorry, but this item is not currently available from your library.

Try another library?
Sign out of this library

Other Topics